Deformation Behavior of Hot Isostatic Pressing FGH96 Superalloy

被引：2

作者：

刘玉红 ^{[1
]}

李付国 ^{[2
]}

喻宏波 ^{[1
]}

机构：

[1] School of Mechanical Engineering Tianjin University, Tianjin 300072, China

[2] School of Materials Science and Engineering Northwestern Polytechnjcal University, Xi'an 710072, China

来源：

Transactions of Tianjin University | 2006年 / 04期

关键词：

powder metallurgical superalloy; hot isostatic pressing; compression testing; mathematical model; regression analysis;

D O I：

暂无

中图分类号：

TG132.3 [特种热性质合金];

学科分类号：

摘要：

The deformation behavior of hot isostatic pressing (HIP) FGH96 superalloy was characterized in the temperature range of 1 000-1 100℃and strain rate range of 0.001-0.1s-1 using hot compression testing. The flow curves of HIP FGH96 superalloy during hot deformation was analyzed systematically. The results show that deformation temperature, strain rate and strain are the main influence factors on flow stress of HIP FGH96 superalloy during hot deformation. The flow stress displays a peak at a critical strain and then decreases with further increase in strain. For a given strain, the flow stress decreases with the increase of deformation temperature, and increases with the increase of strain rate. A mathematical model of these flow curves was established through regression analysis and taking the strain as a modification factor. The calculated stress values agree well with the experimental values.

引用

页码：281 / 285

页数：5

共 50 条

[11] Recrystallization Characterization of FGH96 Superalloy
Ning Yongquan
Li Hui
Yao Zekun
Guo Hongzhen
RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (05) : 1225 - 1229
[12] Investigation on hot deformation behavior of P/M Ni-base superalloy FGH96 by using processing maps
Ning, Yongquan
Yao, Zekun
Guo, Hongzhen
Fu, M. W.
Li, Hui
Xie, Xinghua
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (26): : 6794 - 6799
[13] Deformation Behavior of Superalloy Powder Compact under Hot Isostatic Pressing
Qu, Zonghong
Zhang, Pingxiang
Liang, Shujin
Lai, Yunjin
Luo, Cheng
ADVANCED ENGINEERING MATERIALS, 2020, 22 (11)
[14] Creep Behavior of FGH96 Superalloy at Different Service Conditions
Peng Zichao
Liu Peiyuan
Wang Xuqing
Luo Xuejun
Liu Jian
Zou Jinwen
ACTA METALLURGICA SINICA, 2022, 58 (05) : 673 - 682
[15] Effect of powder preparation technology on the hot deformation behavior of HIPed P/M nickel-base superalloy FGH96
Zhang, M. J.
Li, F. G.
Wang, S. Y.
Liu, C. Y.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (12): : 4030 - 4039
[16] Determining processing maps of FGH96 superalloy
Zhang, Renpeng
Li, Fuguo
Wang, Xiaona
Xibei Gongye Daxue Xuebao/Journal of Northwestern Polytechnical University, 2007, 25 (05): : 652 - 656
[17] Thermal evolution behavior of carbides and γ′ precipitates in FGH96 superalloy powder
Zhang, Lin
Liu, Hengsan
He, Xinbo
Rafi-ud-din
Qu, Xuanhui
Qin, Mingli
Li, Zhou
Zhang, Guoqing
MATERIALS CHARACTERIZATION, 2012, 67 : 52 - 64
[18] Microstructure and mechanical properties of hot extruded FGH96 powder metallurgy superalloy
Liu, Xiao-Tao
Ding, Han-Hui
Yang, Chuan
Liu, Feng
Huang, Lan
Jiang, Liang
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2016, 26 (02): : 354 - 364
[19] Simulation of the FGH96 superalloy microstructural changes under different deformation conditions
Wang, Xiaona
Li, Fuguo
Liu, Yuhong
PHYSICAL AND NUMERICAL SIMULATION OF MATERIALS PROCESSING, PTS 1 AND 2, 2008, 575-578 : 455 - 461
[20] The adjustability of hot workability of FGH96 superalloy toward the effect of oxygen on the microstructure
Zhao, Weiwei
Liu, Na
Li, Zhou
Zhang, Sha
Zhang, Peng
Liu, Yufeng
Zhang, Lin
Qu, Xuanhui
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2025, 929

← 1 2 3 4 5 →