The Influence of Mo Additive on the Microstructure and Property of Ti/Al2O3 Composite

The influence of Mo on the microstructure,bending strength and HV of Ti/Al 2O 3 composite was studied,and the influence mechanism was analyzed.The results indicate that after the addition of Mo,the composite organization is finer and phases distribution is better-proportioned which make the microstructure denser,the bending strength and HV of composite are also increased to a degree.But the bending strength increases first then decreases with the increasing of Mo content,so the appropriate Mo content for the Ti/Al 2O 3 composite is to be further confirmed.