Microstructure and fractal characteristics of the solid-liquid interface forming during directional solidification of Inconel 718

被引：0
|
作者：
WANG Ling 1
2. School of Materials
3. National Key Laboratory of Solidification Technology
机构：
来源：
China Foundry | 2007年 / 03期
基金：
中国国家自然科学基金;
关键词：
Inconel; 718; cooling rate; microstructure; fractal dimension; solid-liquid interface;
D O I：
暂无
中图分类号：
TG244.3 [];
学科分类号：
080201 ; 080503 ;
摘要：
The solidification microstructure and fractal characteristics of the solid-liquid interfaces of Inconel 718,under different cooling rates during directional solidification,were investigated by using SEM. Results showed that 5 μm/s was the cellular-dendrite transient rate. The prime dendrite arm spacing (PDAS) was measured by Image Tool and it decreased with the cooling rate increased. The fractal dimension of the interfaces was calculated and it changes from 1.204310 to 1.517265 with the withdrawal rate ranging from 10 to 100 μm/s. The physical significance of the fractal dimension was analyzed by using fractal theory. It was found that the fractal dimension of the dendrites can be used to describe the solidification microstructure and parameters at low cooling rate,but both the fractal dimension and the dendrite arm spacing are needed in order to integrally describe the evaluation of the solidification microstructure completely.
引用
收藏
页码：182 / 185
页数：4
相关论文
共 50 条
  • [41] Model for particle capture by the solid-liquid interface during solidification of metal matrix nanocomposites
    Jegatheesan, M.
    Bhattacharya, Anirban
    THERMAL SCIENCE AND ENGINEERING PROGRESS, 2023, 45
  • [42] Homogeneous nucleation ahead of the solid-liquid interface during rapid solidification of binary alloys
    Smith, PM
    Elmer, JW
    ACTA MATERIALIA, 1996, 44 (10) : 4217 - 4224
  • [43] APPLICATION OF VIBRATIONAL PARAMETERS TO LOCATE THE SOLID-LIQUID INTERFACE DURING SOLIDIFICATION AND MELTING OF METALS
    WANG, FQ
    ZHU, ZH
    CHEN, SY
    JOURNAL OF MATERIALS SCIENCE, 1993, 28 (15) : 4212 - 4216
  • [44] Departure of Nitrogen Bubbles at the Solid-Liquid Interface during the Solidification of Duplex Stainless Steels
    Wang, Qian
    Xing, Chenyang
    Wang, Rui
    Luo, Peng
    Wang, Bo
    Zhang, Jieyu
    Ma, Jie
    METALS, 2022, 12 (11)
  • [45] A relook at the preferred growth direction of the solid-liquid interface during solidification of pure metals
    Chattopadhyay, C.
    Sangal, S.
    Mondal, K.
    ACTA MATERIALIA, 2010, 58 (16) : 5342 - 5353
  • [46] Effect of hysteresis of solid-liquid interface during solidification on initial transient solute redistribution
    Weidong, Huang, 1600, (07):
  • [47] Thermal oscillation modes of the solid-liquid interface solidification and melting
    Agop, M
    Nica, P
    Carcea, I
    MATERIALS TRANSACTIONS JIM, 2001, 42 (02): : 197 - 206
  • [48] MICROSTRUCTURE AND MECHANICAL PROPERTIES OF HEAT TREATMENT LASER SOLID FORMING SUPERALLOY INCONEL 718
    Song Kan
    Yu Kai
    Lin Xin
    Chen Jing
    Yang Haiou
    Huang Weidong
    ACTA METALLURGICA SINICA, 2015, 51 (08) : 935 - 942
  • [49] Microstructure and mechanical properties of heat treatment laser solid forming superalloy Inconel 718
    Song, Kan
    Yu, Kai
    Lin, Xin
    Chen, Jing
    Yang, Haiou
    Huang, Weidong
    Jinshu Xuebao/Acta Metallurgica Sinica, 2015, 51 (08): : 935 - 942
  • [50] EFFECT ON MICROSTRUCTURE OF FREEZING WITH A SCRAPED SOLID-LIQUID INTERFACE
    PFANN, WG
    CARIDES, JN
    MATERIALS RESEARCH BULLETIN, 1970, 5 (01) : 31 - &
12345