Static coarsening behaviour of lamellar microstructure in selective laser melted Ti–6Al–4V

被引：9

作者：

Sheng Cao ^{[1
,2
]}

Qiaodan Hu ^{[3
]}

Aijun Huang ^{[1
,2
]}

Zhuoer Chen ^{[2
]}

Ming Sun ^{[4
]}

Jiahua Zhang ^{[1
]}

Chenxi Fu ^{[2
]}

Qingbo Jia ^{[2
]}

Chao Voon Samuel Lim ^{[2
]}

Rodney R.Boyer ^{[2
]}

Yi Yang ^{[1
]}

Xinhua Wu ^{[2
]}

机构：

[1] School of Materials Science and Engineering,University of Shanghai for Science and Technology

[2] Monash Centre for Additive Manufacturing (MCAM),Monash University

[3] School of Materials Science and Engineering,Shanghai Jiao Tong University

[4] School of Materials Science and Engineering (MCAM),University of Shanghai for Science and Technology

来源：

Journal of Materials Science & Technology | 2019年 / 35卷 / 08期

基金：

中国国家自然科学基金;

关键词：

Selective laser melting; Ti–6Al–4V; Microstructure; Heat treatment;

D O I：

暂无

中图分类号：

TG665 [光能加工设备及其加工]; TG146.23 [];

学科分类号：

080201 ; 080502 ;

摘要：

Static coarsening mechanism of selective laser melted(SLMed) Ti–6Al–4V with a lamellar microstructure was established at temperatures from 700℃ to 950℃. Microstructure evolution revealed that high heat treatment temperature facilitated martensite decomposition and promoted lamellae growth. At each temperature, the growth rate decreased with increasing holding time. The static coarsening behaviour of SLMed Ti–6Al–4V can be interpreted by Lifshitz, Slyozov, and Wagner(LSW) theory. The coarsening coefficient were 0.33, 0.33–0.4, 0.4–0.5 for 700–800℃, 900℃ and 950℃, respectively. This indicated the coarsening mechanism was bulk diffusion at 700–800℃, and a combination of bulk diffusion and interface reaction at 900℃ and 950℃ conditions.

引用

页码：1578 / 1586

页数：9

共 50 条

[31] Ti—6Al—4V合金和TICp/Ti—6Al—4V复合材料的高温力学行为
吴爱珍
中国材料进展, 2000, (01) : 10 - 11
[32] Microstructural and machinability aspects of electron beam melted Ti–6Al–4V with different building orientations
U. C. Alves
A. Hassui
M. F. de Oliveira
P. I. Neto
C. E. H. Ventura
Progress in Additive Manufacturing, 2023, 8 : 131 - 141
[33] Mechanical and microstructural variations in ECAP of Ti–6Al–4V alloy with equiaxed microstructure
Hamid Arabi
Mostafa Ketabchi
S. H. N. Alhosseini
Rare Metals, 2022, 41 : 2732 - 2738
[34] Indentation strain rate sensitivity of laser-powder bed fused and electron beam melted Ti–6Al–4V
Chandra Kaushik, Harish
Shakil, Shawkat Imam
Amirkhiz, Babak Shalchi
Mohammadi, Mohsen
Asadi, Ebrahim
Haghshenas, Meysam
Hadadzadeh, Amir
Vacuum, 2022, 195
[35] Cyclic Oxidation Behavior of the Ti–6Al–4V Alloy
Shangwu Zeng
Aimin Zhao
Haitao Jiang
Xiang Fan
Xiaoge Duan
Xiaoqian Yan
Oxidation of Metals, 2014, 81 : 467 - 476
[36] Erratum to: Solid Particle Erosion Behaviour of Laser Sintered Heat Treated Ti–6Al–4V Alloy
Amit Kumar Singh Chauhan
Mukul Shukla
Abhishek Kumar
Russian Journal of Nondestructive Testing, 2024, 60 (7) : 840 - 840
[37] Effects of Process Parameters on Temperature and Stress Distributions During Selective Laser Melting of Ti–6Al–4V
Hua Li
Maziar Ramezani
Zhan Chen
Sarat Singamneni
Transactions of the Indian Institute of Metals, 2019, 72 : 3201 - 3214
[38] Rolling contact fatigue performance evaluation of Ti–6Al–4V parts processed by selective laser melting
Peng Zhang
David Z. Zhang
Danhua Peng
Zhonghua Li
Zhongfa Mao
The International Journal of Advanced Manufacturing Technology, 2018, 96 : 3533 - 3543
[39] Selective Laser Melting of Single Track on Ti–6Al–4V Powder: Experimentation and Finite Element Analysis
Manowar Hussain
Pranshul Gupta
P. Kumar
A. K. Das
Arabian Journal for Science and Engineering, 2020, 45 : 1173 - 1180
[40] Ti—6Al—4V的超塑性成形
王廷鑫
稀有金属材料与工程, 1977, (05) : 64 - 65

← 1 2 3 4 5 →