Hydrogen Permeation Behavior in Fe3Al-Based Alloy

被引：1
|
作者：
TAN Xiao hua
机构：
来源：
Journal of Shanghai University | 2000年 / 03期
基金：
中国国家自然科学基金;
关键词：
Fe 3Al based alloy; hydrogen diffusivity; hydrogen permeability; activation energy;
D O I：
暂无
中图分类号：
TG13 [合金学与各种性质合金];
学科分类号：
080502 ;
摘要：
Ultra high vacuum gaseous hydrogen permeation experiments on Fe 3Al based alloy were performed in the temperature range of 330～450℃ with an upstream hydrogen pressure between 3.38×10 4 Pa and 7.28×10 4 Pa. The results show that the hydrogen diffusivity and permeability in Fe 3Al based alloy obey Arrhenius relationship in the experimental temperature range and the hydrogen permeation process is controlled by the lattice diffusion of hydrogen at relative high temperature. The activation energy of hydrogen diffusion in the Fe 3Al based alloy was found to be 75 kJ/mol.
引用
收藏
页码：250 / 253
页数：4
相关论文
共 50 条
  • [41] Cr effect on hydrogen embrittlement of Fe3Al-based iron aluminide intermetallics: Surface or bulk effect
    Zamanzade, Mohammad
    Vehoff, Horst
    Barnoush, Afrooz
    ACTA MATERIALIA, 2014, 69 : 210 - 223
  • [42] Improvement of room temperature environmental brittlement of Fe3Al-based alloy by electro-brush plating
    Zhang, Zhonghua
    Sun, Yangshan
    Liu, Guijun
    Jinshu Xuebao/Acta Metallurgica Sinica, 1996, 32 (09):
  • [43] Site preference of alloying elements in Fe3Al-based alloys
    Ni, XD
    Chen, NX
    Shen, J
    Sun, ZQ
    Yang, WY
    JOURNAL OF MATERIALS RESEARCH, 2001, 16 (02) : 344 - 351
  • [44] Site preference of alloying elements in Fe3Al-based alloys
    Xiao Dong Ni
    Nan Xian Chen
    Jiang Shen
    Zu Qing Sun
    Wang Yue Yang
    Journal of Materials Research, 2001, 16 : 344 - 351
  • [45] Effect of carburizing on the mechanical properties of Fe3Al-based alloys
    Ke, Jianhong
    Tu, Jiangping
    Meng, Liang
    Liu, Maosen
    Zhejiang Daxue Xuebao (Ziran Kexue Ban)/Journal of Zhejiang University (Natural Science Edition), 2000, 34 (02): : 211 - 216
  • [46] Creep of Fe3Al-based alloys with vanadium and carbon additions
    Dobes, F.
    Pesicka, J.
    Kratochvil, P.
    INTERMETALLICS, 2016, 74 : 60 - 64
  • [47] Site preference occupation of Ni and V in Fe3Al-based alloys
    Fuks, D
    Dorfman, S
    Liubich, V
    Kutsenko, L
    Mehrer, H
    CROSS-DISCIPLINARY APPLIED RESEARCH IN MATERIALS SCIENCE AND TECHNOLOGY, 2005, 480 : 81 - 87
  • [48] Bulk nanocrystalline Fe3Al-based material prepared by aluminothermic reaction
    La, PQ
    Yang, J
    Cockayne, DJH
    Liu, WM
    Xue, QJ
    Li, YD
    ADVANCED MATERIALS, 2006, 18 (06) : 733 - +
  • [49] Site preference occupation of Co and Mn in Fe3Al-based alloys
    Fuks, D
    Dorfman, S
    Liubich, V
    Kutsenko, L
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 1697 - 1702
  • [50] Slip system determination by rolling texture measurements around the strength peak temperature in a Fe3Al-based alloy
    Kobayashi, S
    Zaefferer, S
    Schneider, A
    Raabe, D
    Frommeyer, G
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 387 : 950 - 954
12345