Effect of Post-weld Heat Treatment on Microstructure and Mechanical Properties of Friction Stir Welded SSM7075 Aluminium Alloy

被引：1
|
作者：
PRAPAS Muangjunburee [1 ]
JENNARONG Naktewan [1 ]
WORAPHOT Prachasaree [2 ]
机构：
[1] Department of Mining and Materials Engineering, Faculty of Engineering, Prince of Songkla University
[2] Department of Civil Engineering, Faculty of Engineering, Prince of Songkla University
来源：
Journal of Wuhan University of Technology(Materials Science) | 2017年 / 32卷 / 06期
关键词：
friction stir welding(FSW); SSM7075 aluminium alloy; post-weld heat treatment(PWHT);
D O I：
暂无
中图分类号：
TG457.14 [铝];
学科分类号：
080201 ; 080503 ;
摘要：
7XXX series aluminium alloys generally present low weldability by fusion welding methods because of the sensitivity to weld solidification cracking, vaporization of strengthening alloys and other defects in the fusion zone. Friction stir welding(FSW) can be deployed successfully with aluminium alloys. We presented the effect of post-weld heat treatment(PWHT) on the microstructure and mechanical properties of SSM7075 joints. Semi solid plates were butt-welded by FSW at a rotation speed of 1110 r/min, welding speeds of 70 and 110 mm/min. Solution treatment, artificial aging, and T6(solution treatment and artificial aging combined) were applied to the welded joints, each with three samples. It was found that the T6 joints at the speed of 70 mm/min yielded the highest tensile strength of 459.23 MPa. This condition best enhanced the mechanical properties of FSW SSM7075 aluminium alloy joints.
引用
收藏
页码：1420 / 1425
页数：6
相关论文
共 50 条
  • [21] Microstructural properties of friction stir welded and post-weld heat-treated 7449 aluminium alloy thick plate
    Sullivan, A.
    Robson, J. D.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 478 (1-2): : 351 - 360
  • [22] Effects of Post-Weld Heat Treatment on the Mechanical Properties of Similar- and Dissimilar-Alloy Friction Stir Welded Blanks
    Zadpoor, Amir Abbas
    Sinke, Jos
    INTERNATIONAL CONFERENCE ON ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES, PTS ONE AND TWO, 2010, 1315 : 929 - +
  • [23] Effect of post-weld natural aging on mechanical and microstructural properties of friction stir welded 6063-T4 aluminium alloy
    Imam, Murshid
    Racherla, Vikranth
    Biswas, Kajal
    MATERIALS & DESIGN, 2014, 64 : 675 - 686
  • [24] Microstructure, mechanical and corrosion behavior of high strength AA7075 aluminium alloy friction stir welds - Effect of post weld heat treatment
    Kumar, P. Vijaya
    Reddy, G. Madhusudhan
    Rao, K. Srinivasa
    DEFENCE TECHNOLOGY, 2015, 11 (04): : 362 - 369
  • [25] Impact of post weld heat treatment on mechanical and microstructural properties of underwater friction stir spot welded 6061 aluminium alloy
    Shekhawat, Ravindra S.
    Nadakuduru, Vijay N.
    MATERIALS TODAY-PROCEEDINGS, 2022, 56 : 2647 - 2652
  • [26] Effects of post-weld heat treatment on microstructure and mechanical properties of linear friction welded Ti2AlNb alloy
    Chen, X.
    Xie, F. Q.
    Ma, T. J.
    Li, W. Y.
    Wu, X. Q.
    MATERIALS & DESIGN, 2016, 94 : 45 - 53
  • [27] The effect of post-weld heat treatment on the mechanical properties of 2024-T4 friction stir-welded joints
    Aydin, Hakan
    Bayram, Ali
    Durgun, Ismail
    MATERIALS & DESIGN, 2010, 31 (05): : 2568 - 2577
  • [28] Effect of post-weld aging treatment on mechanical properties of Tungsten Inert Gas welded low thickness 7075 aluminium alloy joints
    Temmar, M.
    Hadji, M.
    Sahraoui, T.
    MATERIALS & DESIGN, 2011, 32 (06) : 3532 - 3536
  • [29] Effect of cyclic solution treatment on microstructure and mechanical properties of friction stir welded 7075 Al alloy
    Bayazid, S. M.
    Farhangi, H.
    Asgharzadeh, H.
    Radan, L.
    Ghahramani, A.
    Mirhaji, A.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 649 : 293 - 300
  • [30] Effect of Post-weld Heat Treatment on Microstructure and Mechanical Properties of Laser Beam Welded TiAl-based Alloy
    Liu, Jie
    Ventzke, Volker
    Staron, Peter
    Schell, Norbert
    Kashaev, Nikolai
    Huber, Norbert
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2014, 45A (01): : 16 - 28
12345