Giant Stress-impedance Effect in Amorphous and Current Annealed Fe73.5Cu1Nb3Si13.5B9 Ribbons

被引：0
|
作者：
Deren LI
机构：
来源：
JournalofMaterialsScience&Technology | 2002年 / 04期
关键词：
Amorphous ribbon; DC annealing; Electropulsing annealing; High-current-density; Stress-impedance;
D O I：
暂无
中图分类号：
TG156.2 [退火];
学科分类号：
摘要：
The giant stress-impedance (GSI) effect in amorphous and current annealed Fe73.5Cu1Nb3Si13.5B9 ribbons has been investigated. The results showed that the GSI effect changed drastically with annealing techniques and the maximum stress impedance ratio of 350% was obtained after optimal conditions of current annealing. The behaviors of the stress impedance vary with densities of annealing current and the stress longitudinally applied during current annealing. The maximum change of stress impedance existed in the sample annealed by high-current-density electropulsing under applied stress of 100 MPa.
引用
收藏
页码：293 / 294
页数：2
相关论文
共 50 条
  • [41] RADIOFREQUENCY INDUCED EFFECTS IN AMORPHOUS AND NANOCRYSTALLINE FE73.5CU1NB3SI13.5B9
    KOPCEWICZ, M
    JAGIELSKI, J
    GRAF, T
    FRICKE, M
    HESSE, J
    HYPERFINE INTERACTIONS, 1994, 94 (1-4): : 2223 - 2227
  • [42] Thermomagnetic behaviour and structure of nitrided Fe73.5Cu1Nb3Si13.5B9 ribbons.
    Grognet, S
    Atmani, H
    Larguet, N
    Lebertois, JP
    SYNTHESIS AND PROPERTIES OF MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, PTS 1 AND 2 - ISMANAM-96, 1997, 235-2 : 759 - 764
  • [43] STUDY OF THE CRYSTALLIZATION KINETICS IN AMORPHOUS FE73.5CU1NB3SI13.5B9 ALLOY
    CSEREI, A
    JIANG, J
    AUBERTIN, F
    GONSER, U
    JOURNAL OF MATERIALS SCIENCE, 1994, 29 (05) : 1213 - 1216
  • [44] The Tiny Stress Impedance Effect of Fe73.5Cu1Nb1.5Si13.5B9Mo1.5 Powder/Silicon Rubber Composite Film and Fe73.5Cu1Nb3Si13.5B9 Amorphous Ribbon with Lamellar Structure
    Fu Yuan
    Zhu Zhenghou
    Li Xiaomin
    Zhou Jia
    Zhao Hui
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (02) : 311 - 315
  • [45] Influence of heat treatment on the efficiency of impact fragmentation of amorphous alloy Fe73.5Cu1Nb3Si13.5B9 ribbons
    Kuznetsov P.A.
    Samodelkin E.A.
    Klimov V.N.
    Kashirina A.A.
    Russian Metallurgy (Metally), 2017, 2017 (4) : 293 - 297
  • [46] MAGNETIC-ANISOTROPY IN AS-QUENCHED AND STRESS-ANNEALED AMORPHOUS AND NANOCRYSTALLINE FE73.5CU1NB3SI13.5B9 ALLOYS
    KRAUS, L
    ZAVETA, K
    HECZKO, O
    DUHAJ, P
    VLASAK, G
    SCHNEIDER, J
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1992, 112 (1-3) : 275 - 277
  • [47] The giant magnetoelectric effect in Fe73.5Cu1Nb3Si13.5B9/PZT thick film composites
    Qiu, Jing
    Wen, Yumei
    Li, Ping
    Chen, Hengjia
    JOURNAL OF APPLIED PHYSICS, 2015, 117 (17)
  • [48] Effect of quenching rate on spin texture in amorphous Fe73.5Cu1Nb3Si13.5B9 alloys
    D.A. Univ, Indore, India
    J Magn Magn Mater, 3 (241-244):
  • [49] The influence of the mesoscopic structure of Fe73.5Cu1Nb3Si13.5B9 powder on its giant magneto-impedance effect
    Yang Quanmin
    Xu Qiming
    Fang Yunzhang
    Wang Lingling
    Chen Tao
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 (12) : 2124 - 2127
  • [50] Theoretical study on the influence of the microstructure of Fe73.5Cu1Nb3Si13.5B9 on its giant magneto-impedance effect
    Yang, QM
    Wang, LL
    Sun, DC
    ACTA PHYSICA SINICA, 2005, 54 (12) : 5730 - 5737
12345