Synthesis and characterization of imide modified poly(dimethylsiloxane) with maleopimaric acid as raw material

被引：0

作者：

Tao Xu ^{[1
,2
]}

He Liu ^{[1
]}

Jie Song ^{[3
]}

Shi-Bin Shang ^{[1
]}

Zhan-Qian Song ^{[1
]}

Xiu-Jie Chen ^{[2
]}

Chong Yang ^{[2
]}

机构：

[1] Institute of Chemical Industry of Forestry Products,Chinese Academy of Forestry,Key Laboratory of Biomass Energy and Material,National Engineering Laboratory for Biomass Chemical Utilization,Key and Open Laboratory on Forest Chemical Engineering,SFA

[2] Department of Chemistry and Biochemistry,University of Michigan-Flint

来源：

Chinese Chemical Letters | 2015年 / 26卷 / 05期

基金：

中国国家自然科学基金;

关键词：

Maleopimaric acid; Imide; Polysiloxane; Curing kinetics; Differential scanning calorimetry(DSC);

D O I：

暂无

中图分类号：

TQ330.1 [基础理论];

学科分类号：

0805 ; 080502 ;

摘要：

With the natural rosin derivative（maleopimaric acid,MPA） as the raw material,imide modified vinyl poly（dimethylsiloxane）(MP-VMS) was synthesized and characterized by;H NMR and;C NMR.The curing kinetic parameters of MP-VMS were determined by differential scanning calorimetry（DSC） at various heating rates（5,8,10,15 ℃/min） from the Kissingner.Ozawa and Crane methods.The activation energy（E;）,pre-exponential factor（A） and reaction order（n） were respectively 18.6 kJ/mol,71,108 and0.902.The low-temperature and high-temperature resistance of its curing product were respectively investigated by DSC and thermogravimetric analysis.The results showed that incorporation of MPA could significantly improve the thermal stability of silicone while had no effect on the low-temperature resistance,and the T;（the temperature corresponding to the maximum weight loss rate） increased by 70.7 C.

引用

页码：572 / 574

页数：3

共 50 条

[31] SYNTHESIS AND CHARACTERIZATION OF POLY(DIMETHYLSILOXANE) BASED LIQUID-CRYSTALS
ALLEN, RC
WILKES, GL
YILGOR, I
WU, D
MCGRATH, JE
MAKROMOLEKULARE CHEMIE-MACROMOLECULAR CHEMISTRY AND PHYSICS, 1986, 187 (12): : 2909 - 2931
[32] Synthesis and characterization of UV-curable poly(dimethylsiloxane) dimethacrylate
Thavornyutikarn, Boonlom
Janvikul, Wanida
MACROMOLECULAR SYMPOSIA, 2008, 264 : 144 - 148
[33] SYNTHESIS AND CHARACTERIZATION OF POLY(DIMETHYLSILOXANE) BASED LIQUID-CRYSTALS
ALLEN, RC
YILGOR, I
WU, D
WILKES, GL
MCGRATH, JE
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1983, 186 (AUG): : 132 - POLY
[34] Synthesis, Characterization and Material Application of Poly(ester-oxysilane-imide)s Having Epoxy Residues
Patel, Hasmukh S.
Patel, Bhupendra P.
Patel, Divyesh B.
POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2010, 49 (04) : 394 - 399
[35] Synthesis and thermal crosslinking of benzophenone-modified poly(dimethylsiloxane)s
Mabry, JM
Weber, WP
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2004, 42 (21) : 5514 - 5522
[36] Synthesis and characterization of new type soluble poly(amide-imide)s based on 6FDA imide modified polyterephthalamides
Yang, CP
Chen, RS
Chen, SH
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2001, 39 (01) : 93 - 104
[37] SYNTHESIS AND CHARACTERIZATION OF IMIDE CONTAINING DIISOCYANATES AND POLY(IMIDE-URETHANE)S THEREFROM
AVADHANI, CV
WADGAONKAR, PP
KHISTI, RS
GUNJIKAR, VG
VERNEKAR, SP
POLYMER BULLETIN, 1990, 23 (02) : 163 - 169
[38] Library synthesis and characterization of 3-aminopropyl-terminated poly(dimethylsiloxane)s and poly(ε-caprolactone)-b-poly(dimethylsiloxane)s
Ekin, Abdullah
Webster, Dean C.
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2006, 44 (16) : 4880 - 4894
[39] The synthesis and characterization of poly(2-vinylpyridine)-poly(dimethylsiloxane) and poly(4-vinylpyridine)-poly(dimethylsiloxane) block copolymers via anionic polymerization
Lee, JA
HogenEsch, TE
ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1996, 211 : 96 - POLY
[40] Synthesis and characterization of fluorinated poly(imide siloxane) block copolymers
Ghosh, Anindita
Banerjee, Susanta
Komber, Hartmut
Schneider, Konrad
Haeussler, Liane
Voit, Brigitte
EUROPEAN POLYMER JOURNAL, 2009, 45 (05) : 1561 - 1569

← 1 2 3 4 5 →