Plasmon-enhanced Performance of Dye-sensitized Solar Cells Based on Electrodeposited Ag Nanoparticles

In the present work,pulse current deposition is used to deposit evenly distributed and uniformly sized Ag nanoparticles onto a TiO;nanotube array as photoelectrode in dye-sensitized solar cells（DSSCs）,and the size and amount of loading Ag nanoparticles are controlled by the pulse deposition time.Due to the enhanced light absorption and electron—hole separation caused by plasmon effect,DSSCs based on Ag-modified TiO;nanotube arrays show higher energy conversion efficiencies than those based on bare nanotubes with the same tube length.Particularly,DSSC based on nanotubes modified using pulse deposition time 1 s/3 s delivers the highest energy conversion efficiency of 1.68%and the largest short-circuit current of 4.37 mA/cm;,while DSSC consisting of bare nanotubes exhibits efficiency of 1.20%and short-circuit current of2.27 mA/cm;,which represents a 40%enhancement of cell efficiency in DSSC based on Ag-modified TiO;nanotubes.It is also noted that overly long pulse deposition time will not further increase DSSC efficiency due to agglomeration of Ag particles.For example,when the pulse deposition time is increased to 2 s/6 s,DSSC based on Ag-modified nanotubes exhibits a lower efficiency of 1.42%.Moreover,high-concentration TiCl;treatment on TiO;nanotube arrays can further increase the energy conversion efficiencies to 3.82%and2.61%for DSSC based on Ag-modified TiO;nanotubes and DSSC based on bare TiO;nanotubes,respectively,by significantly creating more surface area for dye loading.