Effect and mechanism of Li content on the corrosion resistance of Al-Li alloy

被引：0

作者：

Han, Chao ^{[1
]}

Yu, Mei ^{[1
]}

Xiao, Jian ^{[1
]}

Yang, Zhong ^{[1
]}

Zhao, Zhenjiang ^{[1
]}

Jia, Xuejiao ^{[1
]}

Li, Songmei ^{[1
]}

Liu, Jianhua ^{[1
]}

机构：

[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China

来源：

CORROSION SCIENCE | 2025年 / 246卷

关键词：

Al-Li alloy; Corrosion product layer; Electrochemical behavior; Diffusion; Cathodic reduction reaction; LOCALIZED CORROSION; OXIDE-FILMS; IMPEDANCE; BEHAVIOR;

D O I：

10.1016/j.corsci.2025.112768

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of Li content (0.5 wt%, 1.0 wt%, 1.5 wt% and 2.0 wt%) on corrosion resistance of Al-Li alloy was studied in 3.5 wt% NaCl. The corrosion resistance is affected by changes in the characteristics of the corrosion product layer caused by variations in Li content. The alloy with 1.5 wt% Li exhibited the best corrosion resistance, which is attributed to Li2CO3 generated on its surface. Li2CO3 layer acted as a barrier to corrosive Cl- and O2. The wide bandgap of Li2CO3 hindered the transfer of electrons, increasing the resistance of cathodic reaction and retarding further corrosion.

引用

页数：14

共 50 条

[21] Effect of Aging Treatment on Corrosion Resistance of Al-Li Alloy Joint Welded by Electron Beam Welding
Wang Shaogang
Huang Yan
Zhao Li
RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (07) : 1973 - 1979
[22] Effect of Aging Treatment on Corrosion Resistance of Al-Li Alloy Joint Welded by Electron Beam Welding
Wang, Shaogang
Huang, Yan
Zhao, Li
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2018, 47 (07): : 1973 - 1979
[23] Effect of Thermo-Mechanical Processing on Microstructure and Corrosion Resistance of 2099 Al-Li Alloy Extrusions
Zhang Zhenqiang
Xu Xiaojing
Song Tao
Zhang Yunkang
Luo Yong
Wu Yao
Deng Ping'an
RARE METAL MATERIALS AND ENGINEERING, 2013, 42 (12) : 2619 - 2624
[24] Mechanism of cryorolling and aging treatment for enhancing corrosion properties of 2195 Al-Li alloy
Xiao, Yue
Wang, Wen-shuai
Farid, Waqas
Zhang, Li-hua
Kong, Charlie
Yu, Hai-liang
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2025, 35 (01) : 13 - 29
[25] Effect of temperature on the fracture mechanisms of 8090 Al-Li alloy and 8090 Al-Li/SiC composite
González, C
Martín, A
Llorca, J
SCRIPTA MATERIALIA, 2004, 51 (11) : 1111 - 1115
[26] Corrosion behavior and stress corrosion cracking resistance of Al-Li alloys
Ohsaki, Shuhei
Takahashi, Tsuneo
Keikinzoku/Journal of Japan Institute of Light Metals, 1991, 41 (04):
[27] Effect of current pulse on mechanism of superplastic deformation of 2091 Al-Li alloy
Liu, Zhiyi
Liu, Bing
Deng, Xiaotie
Lei, Yi
Cui, Jianzhong
Bai, Guangrun
Jinshu Xuebao/Acta Metallurgica Sinica, 2000, 36 (09): : 944 - 951
[28] EFFECT OF LI LOSS ON SOME PHYSICAL-PROPERTIES OF AL-LI ALLOY
ELSALAM, FA
EATAH, AI
TAWFIK, A
PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1983, 75 (02): : 379 - 384
[29] EFFECT OF SCRATCHES ON THE FATIGUE BEHAVIOR OF AN AL-LI ALLOY
INCHEKEL, A
TALIA, JE
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (05) : 501 - 507
[30] Effect of Laser Power on Corrosion Properties of Hybrid Welded 2195 Al-Li Alloy
Yang, Mei
Yang, Honglang
Yang, Lie
Liu, Yang
Tan, Jian
Chen, Jin
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01): : 280 - 292

← 1 2 3 4 5 →