Phase equilibria of the Tb-Fe-B system at 1000, 900 and 800 °C

被引：0
|
作者：
Qiu, Chengliang [1 ]
Liu, Shuhong [1 ]
Yang, Wei [1 ]
Mei, Jiacheng [1 ]
Zhai, Wei [2 ]
Du, Yong [1 ]
机构：
[1] Cent South Univ, Natl Key Lab Sci & Technol High Strength Struct Ma, Changsha 410083, Peoples R China
[2] Northwestern Polytech Univ, Sch Phys Sci & Technol, Xian 710072, Peoples R China
来源：
MATERIALS CHARACTERIZATION | 2025年 / 222卷
关键词：
Tb-Fe-B; Phase equilibria; Isothermal sections; Ternary compounds; RARE-EARTH; DY; INTERMETALLICS; DIFFRACTION; BORIDES; LU; GD; ER; ND; HO;
D O I：
10.1016/j.matchar.2025.114793
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Phase equilibria of the Tb-Fe-B system were investigated at 1000, 900 and 800 degrees C using X-ray diffraction (XRD) and electron probe microanalysis (EPMA) on annealed alloys with a B content <= 50 at.%. Isothermal sections at 1000, 900 and 800 degrees C were then proposed, revealing the similar phase equilibria except for the phase regions containing liquid, which originates from the binary Fe-Tb system at 900 and 1000 degrees C. Five ternary compounds of Tb2Fe14B, TbFe4B4, Tb5Fe2B6, Tb3FeB7 and TbFeB4 were observed to be stoichiometric and the solubilities of Tb in Fe-B, Fe in Tb-B and B in Tb-Fe binary phases were measured to be negligible. Additionally, the ternary compound TbFe2B2 was not detected in this work.
引用
收藏
页数：9
相关论文
共 50 条
  • [31] Phase Equilibria in the Fe-Al-Nb(-B) System at 700 °C
    Gedsun, A.
    Stein, F.
    Palm, M.
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2022, 43 (04) : 409 - 418
  • [32] Phase Equilibria in the Fe-Al-Nb(-B) System at 700 °C
    A. Gedsun
    F. Stein
    M. Palm
    Journal of Phase Equilibria and Diffusion, 2022, 43 : 409 - 418
  • [33] Evolution of crystallographic alignment in Tb-Fe-B melt-spun ribbons
    刘荣明
    陈静武
    邓韵文
    那冉
    刘卫强
    岳明
    张久兴
    Journal of Rare Earths, 2010, 28(S1) (S1) : 382 - 384
  • [34] Evolution of crystallographic alignment in Tb-Fe-B melt-spun ribbons
    Liu Rongming
    Chen Jingwu
    Deng Yunwen
    Na Ran
    Liu Weiqiang
    Yue Ming
    Zhang Jiuxing
    JOURNAL OF RARE EARTHS, 2010, 28 : 382 - 384
  • [35] An investigation of the Al-Cu-Cr phase diagram:: Phase equilibria at 800-1000°C
    Grushko, B.
    Kowalska-Strzeciwilk, E.
    Przepiorzynski, B.
    Surowiec, M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2006, 417 (1-2) : 121 - 126
  • [36] An investigation of the Al-Cu-Cr phase diagram: Phase equilibria at 800-1000 °C
    Grushko, B.
    Kowalska-Strzeciwilk, E.
    Przepiórzyński, B.
    Surowiec, M.
    Journal of Alloys and Compounds, 2006, 417 (1-2): : 121 - 126
  • [37] Phase equilibria in the Ni-Al-W system at 900°C
    Broz, P
    Bursík, J
    Stará, Z
    MONATSHEFTE FUR CHEMIE, 2005, 136 (11): : 1915 - 1920
  • [38] Phase Equilibria in the Al-Ga-As-Bi System at 900°C
    Khvostikov, V. P.
    Khvostikova, O. A.
    Potapovich, N. S.
    Vlasov, A. S.
    INORGANIC MATERIALS, 2023, 59 (07) : 691 - 695
  • [39] Phase equilibria of the system La2O3-NiO-Li2O at 700, 800, and 900°C
    Li, GB
    Yang, JQ
    Fan, YX
    Tian, SJ
    Zheng, CG
    JOURNAL OF SOLID STATE CHEMISTRY, 1998, 141 (02) : 457 - 461
  • [40] PHASE-RELATIONS IN THE SYSTEM GA-FE-S AT 900-DEGREES-C AND 800-DEGREES-C
    UENO, T
    SCOTT, SD
    CANADIAN MINERALOGIST, 1994, 32 : 203 - 210
12345