Mechanical properties of Cu/Cu-Al laminated alloys with gradient interface affected zone

被引:0
|
作者
Liu, Shuaibo [1 ]
Gu, Ji [1 ]
Song, Min [1 ]
机构
[1] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Peoples R China
基金
中国国家自然科学基金;
关键词
Cu; Heterostructure; Powder metallurgy; Strength; Transmission electron microscopy; DEFORMATION-BEHAVIOR; DUCTILITY; SIZE; STRENGTH; CU;
D O I
10.1557/s43578-025-01517-7
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this work, four types of laminated Cu-Al alloys with the same total thickness but varying numbers of layers were fabricated using a combination of powder metallurgy and hot rolling techniques. Due to the element diffusion caused by sintering and hot rolling, a gradient interface region, also called interface affected zone (IAZ), with a width of about 70-110 mu m was formed between the Cu layer and the Cu-6Al layer. The results suggest that compared to the homogeneously mixed Cu/Cu-6Al alloy, the laminated alloy exhibits higher mechanical properties. Especially, the laminated alloy with more layers and smaller interface spacing shows superior mechanical properties. The IAZ can effectively relieve the stress concentration at the interface and thus provide continuous work hardening ability. Furthermore, the heterogeneous deformation-induced (HDI) strengthening was enhanced by adjusting the interface spacing and the width of the IAZ, so as to achieve a synergistic enhancement of strength and ductility.
引用
收藏
页码:560 / 571
页数:12
相关论文
共 50 条
  • [31] Effect of palladium on the mechanical properties of Cu-Al intermetallic compounds
    20150300423851
    Lim, Adeline B.Y., 1600, Elsevier Ltd (628):
  • [32] Kinetics of eutectoid decomposition in Cu-Al and Cu-Al-Ag alloys
    Arruda, GJ
    Adorno, AT
    Magnani, R
    Beatrice, CRS
    MATERIALS LETTERS, 1997, 32 (2-3) : 79 - 84
  • [33] PHASE-TRANSFORMATIONS IN CU-AL AND CU-ZN-AL ALLOYS
    KWARCIAK, J
    JOURNAL OF THERMAL ANALYSIS, 1986, 31 (03): : 559 - 566
  • [34] SPECIFIC HEATS OF ALPHA-PHASE CU-AL AND DILUTE MAGNETIC CU-AL (FE) ALLOYS
    ZRUDSKY, DR
    DELINGER, WG
    SAVAGE, WR
    SCHWEITZER, JW
    PHYSICAL REVIEW B-SOLID STATE, 1971, 3 (09): : 3025 - +
  • [35] The influence of stacking fault energy on the mechanical properties of nanostructured Cu and Cu-Al alloys processed by high-pressure torsion
    An, X. H.
    Lin, Q. Y.
    Wu, S. D.
    Zhang, Z. F.
    Figueiredo, R. B.
    Gao, N.
    Langdon, T. G.
    SCRIPTA MATERIALIA, 2011, 64 (10) : 954 - 957
  • [36] Cu-Al-Mn Alloys with a Gradient of Properties
    Bubley, I. R.
    Koval, Yu. M.
    Kudryavtsev, Yu. V.
    METALLOFIZIKA I NOVEISHIE TEKHNOLOGII, 2008, 30 (08): : 1109 - 1117
  • [37] MECHANISMS OF ANNEAL HARDENING IN CU-AL ALLOYS
    BADER, M
    ELDIS, GT
    WARLIMONT, H
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (02): : 249 - 255
  • [38] Elemental separation in nanocrystalline Cu-Al alloys
    Wang, Y. B.
    Liao, X. Z.
    Zhao, Y. H.
    Cooley, J. C.
    Horita, Z.
    Zhu, Y. T.
    APPLIED PHYSICS LETTERS, 2013, 102 (23)
  • [39] ASYMMETRIC DISLOCATION NODES IN CU-AL ALLOYS
    PRINZ, F
    KARNTHALER, HP
    KIRCHNER, HOK
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1976, 37 (01): : 223 - 233
  • [40] REMARKS ON STRUCTURE OF MARTENSITES IN CU-AL ALLOYS
    SATO, H
    TOTH, RS
    HONJO, G
    ACTA METALLURGICA, 1967, 15 (08): : 1381 - &