Experimental investigation on the initiation and propagation of corrosion fatigue cracks in EA4T axle steel treated by ultrasonic surface rolling

被引：0
|
作者：
Dongdong Ji [1 ]
Jiwang Zhang [1 ]
Hang Li [1 ]
Kaixin Su [1 ]
机构：
[1] Southwest Jiaotong University,State Key Laboratory of Rail Transit Vehicle System
来源：
Journal of Materials Science | 2025年 / 60卷 / 1期
关键词：
D O I：
10.1007/s10853-024-10523-9
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：604 / 624
页数：20
相关论文
共 50 条
  • [21] Closure Effect of Ⅰ+Ⅱ Mixed-mode Crack for EA4T Axle Steel
    Shuancheng Wang
    Bing Yang
    Shuwei Zhou
    Jian Li
    Shoune Xiao
    Chinese Journal of Mechanical Engineering, 2024, 37 (04) : 340 - 354
  • [22] Microstructure and Fatigue of EA4T Steel in Laser Cladding Remanufacturing
    Chen, Wenjing
    Chen, Qunyan
    Zhang, Zhenlin
    Tang, Sicheng
    Cai, Qing
    COATINGS, 2022, 12 (08)
  • [23] Effects of Different Microstructure on Resistance of EA4T Railway Axle Steel of Equal Strength to Fatigue Crack Growth
    Cerny, Ivo
    Linhart, Vaclav
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE VII, 2014, 592-593 : 631 - 634
  • [24] Fatigue strength assessment of high-speed railway axle EA4T steel with foreign object damage
    Luo, Yan
    Wang, Hui
    Li, Cunhai
    Ren, Xinyan
    Wu, Shengchuan
    ENGINEERING FAILURE ANALYSIS, 2022, 133
  • [25] Effect of Cooling Condition on Fatigue Behavior of the Forged EA4T Steel
    Li, Changyou
    Dai, Weibing
    Liu, Yuzhuo
    Xu, Wenze
    Zhang, Yimin
    Tan, Zhi
    STEEL RESEARCH INTERNATIONAL, 2020, 91 (09)
  • [26] Experimental characterization and numerical modeling on the external impacting of high-speed railway axle EA4T steel
    Zhao, Xin
    Wu, Shengchuan
    Bao, Jianguang
    Ao, Ni
    Peng, Wenjie
    Sun, Wei
    ENGINEERING FAILURE ANALYSIS, 2021, 125
  • [27] Effect of micro-shot peening, conventional shot peening and their combination on fatigue property of EA4T axle steel
    Li, Xing
    Zhang, Jiwang
    Yang, Bing
    Zhang, Jinxin
    Wu, Mingze
    Lu, Liantao
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2020, 275 (275)
  • [28] Effect of specimen geometry on fatigue crack growth rates for the railway axle material EA4T
    Varfolomeev, I.
    Luke, M.
    Burdack, M.
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (05) : 742 - 753
  • [29] Inductive surface layer treatment to increase the corrosion fatigue strength of the wheelset shaft material EA4T
    Schoenborn, S.
    Melz, T.
    Hasnain, J.
    Scheerer, H.
    Engler, T.
    Oechsner, M.
    Schulz, A.
    Steinbacher, M.
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2024, 55 (06) : 733 - 750
  • [30] Propagation of surface initiated rolling contact fatigue cracks in bearing steel
    Rycerz, Pawel
    Olver, Andrew
    Kadiric, Amir
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 97 : 29 - 38
12345