Influence of high-energy ball-milling duration on Nb-Al powder mixture microhardness

被引：0

作者：

D. A. Osipov ^{[1
]}

A. D. Ishkov ^{[2
]}

I. V. Smirnov ^{[2
]}

K. V. Grinyaev ^{[1
]}

I. A. Ditenberg ^{[2
]}

机构：

[1] Russian Academy of Sciences,Institute of Strength Physics and Materials Science of the Siberian Branch

[2] National Research Tomsk State University,undefined

来源：

Russian Physics Journal | 2024年 / 67卷 / 10期

关键词：

Niobium-aluminum powder system; High-energy ball milling; Microhardness; 538.911; 669-179;

D O I：

10.1007/s11182-024-03287-x

中图分类号：

学科分类号：

摘要：

The influence of high-energy ball milling duration on the microhardness values of the precursors from the Nb–Al powder mixture is studied. The main stages of microhardness increase, characterized by the specificity of its values change relative to the HEBM duration, are identified. As the microhardness values increase, an increase in the spread of its values is observed, which indicates the heterogeneity of the structural-phase state. Structural investigation methods have established that after 3.5 min HEBM an ordered AlNb2 compound is formed, the volume fraction of which is about 4%. It is assumed that the presence of particles of a strong ordered phase makes the main contribution to the strengthening of the powder mixture precursor.

引用

页码：1599 / 1602

页数：3

共 50 条

[41] High-energy ball-milling of FeAl2 and Fe2Al5 intermetallic systems
Romero-Romero, J. R.
Luis Lopez-Miranda, J.
Esparza, R.
Espinosa-Medina, M. A.
Rosas, G.
STRUCTURAL AND CHEMICAL CHARACTERIZATION OF METALS, ALLOYS AND COMPOUNDS, 2013, 755 : 47 - +
[42] Synthesis of single-phase Al-Cu-Fe quasicrystals using high-energy ball-milling
Turquier, F.
Cojocaru, V. D.
Stir, M.
Nicula, R.
Burkel, E.
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2007, 353 (32-40) : 3417 - 3420
[43] High-energy ball milling of Al-based alloys
Rodríguez, CAD
Botta , WJ
ADVANCED POWDER TECHNOLOGY II, 2001, 189-1 : 573 - 577
[44] Phase formation during high-energy ball milling of the 33Al-45Cu-22Fe (at.%) powder mixture
Tikhov, Serguei F.
Valeev, Konstantin R.
Salanov, Aleksey N.
Cherepanova, Svetlana V.
Boldyreva, Natalya N.
Zaikovskii, Vladimir I.
Sadykov, Vladislav A.
Dudina, Dina V.
Lomovsky, Oleg I.
Romanenkov, Vladimir E.
Pyatsyushik, Evgenii E.
JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 736 : 289 - 296
[45] BN/Al composite formation by high-energy ball milling
Du, YJ
Li, SY
Zhang, K
Lu, K
SCRIPTA MATERIALIA, 1997, 36 (01) : 7 - 14
[46] Production of Nanosized Boron Oxide Powder by High-Energy Ball Milling
Alizadeh, Mohammad
Sharifianjazi, Fariborz
Haghshenasjazi, Ehsan
Aghakhani, Masood
Rajabi, Laleh
SYNTHESIS AND REACTIVITY IN INORGANIC METAL-ORGANIC AND NANO-METAL CHEMISTRY, 2015, 45 (01) : 11 - 14
[47] The compressibility of Cu/SiCp powder prepared by high-energy ball milling
Gan, Keke
Gu, Minyuan
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 199 (1-3) : 173 - 177
[48] High-energy ball milling of powder B-C mixtures
Ramos, Alfeu S.
Taguchi, Simone P.
Ramos, Erika C. T.
Arantes, Vera L.
Ribeiro, Sebastiao
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 422 (1-2): : 184 - 188
[49] Low-temperature densification of nano Si-C powder containing Al-C additives prepared by high-energy ball-milling
Yoon, Bola
Lee, Sea-Hoon
Lee, HeeSoo
CERAMICS INTERNATIONAL, 2017, 43 (01) : 12 - 19
[50] DILATOMETRY OF NI3AL POWDER DISORDERED BY BALL-MILLING
GIALANELLA, S
DELORENZO, R
MARINO, F
GUELLA, M
INTERMETALLICS, 1995, 3 (01) : 1 - 8

← 1 2 3 4 5 →