Effect of heat input on microstructure and mechanical properties of weld metal of 690 MPa grade HSLA steel

被引：0
|
作者：
Tang, Cunjiang [1 ,2 ]
An, Tongbang [2 ]
Peng, Yun [2 ]
Lin, Chuncheng [2 ,3 ]
Ma, Chengyong [2 ]
Liu, Xuming [1 ]
机构：
[1] Ansteel Beijing Research Institute Co., Ltd., Beijing,102209, China
[2] Central Iron and Steel Research Institute, Beijing,100081, China
[3] College of Mechanical and Electrical Engineering, Beijing University of Chemical Technology, Beijing,100029, China
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2024年 / 45卷 / 09期
关键词：
D O I：
10.12073/j.hjxb.20230501001
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：110 / 119
相关论文
共 50 条
  • [11] Effect of flux basicity on the microstructure and mechanical properties of an HSLA steel submerged arc weld
    Bhole, SD
    Nemade, JB
    TRENDS IN WELDING RESEARCH, PROCEEDINGS, 2003, : 707 - 712
  • [12] Effect of the temperature of post weld heat treatment on microstructure and performance of weld metal for 1 000 MPa grade high strength steel
    An, Tongbang
    Tian, Zhiling
    Shan, Jiguo
    Peng, Yun
    Wei, Jinshan
    Cui, Bing
    Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2015, 51 (04): : 40 - 46
  • [13] Effect of aluminium element on microstructure and properties of weld metal of 960 MPa steel
    裘荣鹏
    冯旭
    China Welding, 2020, 29 (04) : 48 - 53
  • [14] Microstructure and Mechanical Properties of GMAW Weld Metal of 890MPa Class Steel
    Yun PENG
    Xing-na PENG
    Xiao-mu ZHANG
    Zhi-ling TIAN
    Tao WANG
    Journal of Iron and Steel Research(International), 2014, 21 (05) : 539 - 544
  • [15] Effect of interpass temperature on the microstructure and mechanical properties of multi-pass weld metal in a 550-MPa-grade offshore engineering steel
    X. L. Wang
    Y. T. Tsai
    J. R. Yang
    Z. Q. Wang
    X. C. Li
    C. J. Shang
    R. D. K. Misra
    Welding in the World, 2017, 61 : 1155 - 1168
  • [16] Effect of interpass temperature on the microstructure and mechanical properties of multi-pass weld metal in a 550-MPa-grade offshore engineering steel
    Wang, X. L.
    Tsai, Y. T.
    Yang, J. R.
    Wang, Z. Q.
    Li, X. C.
    Shang, C. J.
    Misra, R. D. K.
    WELDING IN THE WORLD, 2017, 61 (06) : 1155 - 1168
  • [17] Microstructure and properties of 700 MPa grade HSLA steel during high temperature deformation
    Chen, Xizhang (chenxizhang@wzu.edu.cn), 1600, Elsevier Ltd (631):
  • [18] Microstructure and properties of 700 MPa grade HSLA steel during high temperature deformation
    Chen, Xizhang
    Huang, Yuming
    Lei, Yucheng
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 631 : 225 - 231
  • [19] Effect of Austenitizing Temperature on Microstructure and Crystallographic Evolution of 900 MPa Grade HSLA Steel
    Gao, Ye
    Ren, Jiakuan
    Li, Zhifeng
    Cui, Cong
    Chen, Jun
    Liu, Zhenyu
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2022, 36 (01): : 21 - 28
  • [20] Effect of Cr content on the microstructure evolution in weld metal for 1000 MPa grade high strength steel
    Feng, Wei
    Yu, Tingxiang
    Chen, Bo
    Zhang, Qingsu
    Cai, Hongguang
    Zhang, Biying
    Ma, Qiang
    Hanjie Xuebao/Transactions of the China Welding Institution, 2024, 45 (09): : 76 - 83
12345