Longitudinal cracking in a carbon black filled natural rubber vulcanizate during chemical stress relaxation

被引：0
|
作者：
机构：
来源：
Rubber Chem Technol | / 2卷 / 157-167期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Thin specimens of a black-filled, natural rubber vulcanizate have been held in uniaxial tension at 72 °C and 200% elongation in a forced air oven. After substantial oxidative attack (inferred from stress relaxation), small edge cracks formed. Initially, these cracks grew perpendicular to the loading direction, but, upon reaching about 0.1 mm in depth, longitudinal crack growth commenced and fracture progressed by a kind of 0°-peel process with `splitting-off' of successive strands of rubber. This phenomenon is attributed to anisotropy in strength caused both by straining and by oxidative attack.
引用
收藏
相关论文
共 50 条
  • [41] Fracture properties of natural rubber filled with hybrid carbon black/nanoclay
    Yuanbo Liu
    Li Li
    Qi Wang
    Xin Zhang
    Journal of Polymer Research, 2011, 18 : 859 - 867
  • [42] Flocculation and Viscoelastic Behaviour in Carbon Black-Filled Natural Rubber
    Tunnicliffe, Lewis B.
    Kadlcak, Jakub
    Morris, Michael D.
    Shi, Ye
    Thomas, Alan G.
    Busfield, James J. C.
    MACROMOLECULAR MATERIALS AND ENGINEERING, 2014, 299 (12) : 1474 - 1483
  • [43] Fracture properties of natural rubber filled with hybrid carbon black/nanoclay
    Liu, Yuanbo
    Li, Li
    Wang, Qi
    Zhang, Xin
    JOURNAL OF POLYMER RESEARCH, 2011, 18 (05) : 859 - 867
  • [44] Insight into the weak strain overshoot of carbon black filled natural rubber
    Fan, Xinpeng
    Xu, Huilong
    Zhang, Qingxu
    Xiao, Di'e
    Song, Yihu
    Zheng, Qiang
    POLYMER, 2019, 167 : 109 - 117
  • [45] Tea waste/carbon black hybrid filled natural rubber composites
    Hayeemasae, Nabil
    Ismail, Hanafi
    MALAYSIAN JOURNAL OF FUNDAMENTAL AND APPLIED SCIENCES, 2020, 16 (06): : 366 - 370
  • [46] Mechanical Properties of Silicon Carbon Black Filled Natural Rubber Elastomer
    Qian Miaomiao
    Sui Jiayang
    Wang Xiaofeng
    Zhu Yanchao
    CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 2019, 35 (01) : 139 - 145
  • [47] Effect of carbon black on the fatigue crack growth in filled natural rubber
    Yao, Hong
    Weng, Gengsheng
    Liu, Yanpeng
    Chang, Aijun
    Fu, Kun
    Chen, Zhongren
    Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2015, 31 (12): : 78 - 83
  • [48] Effective properties of carbon black filled natural rubber:: Experiments and modeling
    Omnes, B.
    Thuillier, S.
    Pilvin, P.
    Grohens, Y.
    Gillet, S.
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2008, 39 (07) : 1141 - 1149
  • [49] FATIGUE CRACK INITIATION IN A CARBON BLACK-FILLED NATURAL RUBBER
    Huneau, Bertrand
    Masquelier, Isaure
    Marco, Yann
    Le Saux, Vincent
    Noizet, Simon
    Schiel, Clementine
    Charrier, Pierre
    RUBBER CHEMISTRY AND TECHNOLOGY, 2016, 89 (01): : 126 - 141
  • [50] Mechanical Properties of Silicon Carbon Black Filled Natural Rubber Elastomer
    Miaomiao Qian
    Jiayang Sui
    Xiaofeng Wang
    Yanchao Zhu
    Chemical Research in Chinese Universities, 2019, 35 : 139 - 145
12345