Oxidation of low carbon steel in multicomponent gases: Part II. Reaction mechanisms during reheating

被引：1
|
作者：
Abuluwefa, H.T. [1 ]
Guthrie, R.I.L. [1 ]
Ajersch, F. [1 ]
机构：
[1] McGill Univ, Montreal, Canada
来源：
Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science | 1997年 / 28 A卷 / 08期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：1643 / 1651
相关论文
共 50 条
  • [31] Equilibration of plain carbon and alloy steels with endothermic carburizing atmospheres: Part II. Oxidation of plain carbon and Armco steels during carburizing at 1000 °C and 1038 °C
    Jong-Il Hwang
    Tae-Gu Jhee
    Young-Kyu Kim
    Tae-Young Hwang
    Metals and Materials International, 2010, 16 : 693 - 699
  • [32] In situ SEM analysis of surface oxidation mechanisms in carbon steel during vacuum heat treatment
    Heard, Rhiannon
    Siviour, Clive R.
    Dragnevski, Kalin, I
    MATERIALS TODAY-PROCEEDINGS, 2020, 33 : 1898 - 1903
  • [33] Change in carbon content on the surface of a multicomponent catalyst during its reduction, oxidation and due to action of the reaction medium
    B. N. Kuznetsov
    V. M. Perov
    A. M. Alekseyev
    D. L. Astanovsky
    V. I. Yakerson
    Reaction Kinetics and Catalysis Letters, 1999, 67 : 89 - 93
  • [34] Change in carbon content on the surface of a multicomponent catalyst during its reduction oxidation and due to action of the reaction medium
    Kuznetsov, BN
    Perov, VM
    Alekseyev, AM
    Astanovsky, DL
    Yakerson, VI
    REACTION KINETICS AND CATALYSIS LETTERS, 1999, 67 (01): : 89 - 93
  • [35] The Effect of Alternating Current on the Rate of Dissolution of Carbon Steel in a Chloride Electrolyte. Part II. Cathode Potentials
    A. I. Marshakov
    T. A. Nenasheva
    E. V. Kasatkin
    I. V. Kasatkina
    Protection of Metals and Physical Chemistry of Surfaces, 2018, 54 : 1236 - 1245
  • [36] The Effect of Alternating Current on the Rate of Dissolution of Carbon Steel in a Chloride Electrolyte. Part II. Cathode Potentials
    Marshakov, A. I.
    Nenasheva, T. A.
    Kasatkin, E. V.
    Kasatkina, I. V.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2018, 54 (07) : 1236 - 1245
  • [37] Deformation and damage mechanisms of zinc coatings on hot-dip galvanized steel sheets: Part II. Damage modes
    Rodolphe Parisot
    Samuel Forest
    André Pineau
    François Grillon
    Xavier Demonet
    Jean-Michel Mataigne
    Metallurgical and Materials Transactions A, 2004, 35 : 813 - 823
  • [38] Deformation and damage mechanisms of zinc coatings on hot-dip galvanized steel sheets: Part II. Damage modes
    Parisot, R
    Forest, S
    Pineau, A
    Nguyen, F
    Demonet, X
    Mataigne, JM
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (03): : 813 - 823
  • [39] High-temperature oxidation studies of low-nickel austenitic stainless steel.: Part II:: Cyclic oxidation
    Pérez, FJ
    Cristóbal, MJ
    Hierro, MP
    OXIDATION OF METALS, 2001, 55 (1-2): : 165 - 175
  • [40] High-Temperature Oxidation Studies of Low-Nickel Austenitic Stainless Steel. Part II: Cyclic Oxidation
    F. J. Pérez
    M. J. Cristóbal
    M. P. Hierro
    Oxidation of Metals, 2001, 55 : 165 - 175
12345