Mechanism of Ductile Fracture in Ferritic Spheroidal-Graphite Cast Iron.

被引：0

作者：

Qing, Sun Yao

Detraux, J.M.

Touzot, G.

Francois, D.

机构：

来源：

| 1600年 / 80期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

In order to determine the conditions of cavity initiation and growth, causing the ductile fracturing of ferritic spheroidal-graphite cast iron, tensile tests were performed on cylindrical specimens. Numerical calculations by the finite element method revealed the evolution of strains and deformations in these specimens. It is found that cavity initiation occurs when the strain at the interface reaches 600 MPa and that fracturing is controlled by the growth of the cavities.

引用

共 50 条

[21] Fracture Toughness of Flake Graphite Cast Iron.
Grueter, Ludwig
Giessereiforschung, 1977, 29 (02): : 47 - 51
[22] PRACTICAL AND TECHNICAL EXPERIENCE GAINED IN THE PRODUCTION OF HIGH-QUALITY SPHEROIDAL-GRAPHITE IRON.
Mayer, H.
Hammerli, F.
1600, (133):
[23] FEATURES OF FAILURE FOR FERRITIC CAST-IRON WITH SPHEROIDAL GRAPHITE
SMIRNOVA, LN
SHCHEGLYUK, NI
METAL SCIENCE AND HEAT TREATMENT, 1989, 31 (3-4) : 255 - 258
[24] Fracture mechanism of Ferritic Ductile Cast Iron in Extremely Low Cycle Fatigue
Komotori, J
Shimizu, M
LOW CYCLE FATIGUE AND ELASTO-PLASTIC BEHAVIOUR OF MATERIALS, 1998, : 39 - 44
[25] THE EFFECT OF TRIAXIAL STRESS ON DUCTILITY AND FRACTURE MORPHOLOGY OF FERRITIC SPHEROIDAL GRAPHITE CAST-IRON
LIN, YF
LUI, TS
CHEN, LH
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1994, 25 (04): : 821 - 825
[26] INFLUENCE OF SILICON CONTENT ON THE INTERGRANULAR FRACTURE EMBRITTLEMENT OF FERRITIC SPHEROIDAL GRAPHITE CAST-IRON
LUI, TS
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (05): : S524 - S524
[27] Effect of maximum temperature on the cyclic-heating-induced embrittlement of high-silicon ferritic spheroidal-graphite cast iron
Lin, HM
Lui, TS
Chen, LH
MATERIALS TRANSACTIONS, 2004, 45 (02) : 569 - 576
[28] ASPECTS OF SPHEROIDAL-GRAPHITE IRON PRODUCTION.
Anon
Foundry Trade Journal, 1976, 140 (3077): : 65 - 68
[29] An Evaluation of the Tolerable Defect Size and Fracture Mechanism in Spheroidal Graphite Cast Iron
Archiv Metall, 2 (199):
[30] INVESTIGATING INFLUENCE OF HEAT-TREATMENT ON PROPERTIES OF SPHEROIDAL-GRAPHITE CAST-IRON
SOLNTSEV, LA
STEEL IN THE USSR, 1974, 4 (08): : 687 - 688

← 1 2 3 4 5 →