LASER HARDENING OF CRANKSHAFTS MADE OF HIGH STRENGTH CAST IRON.

被引：0
|
作者：
Levchenko, A.A.
Tananko, I.A.
Guiva, R.T.
Guiva, V.A.
Kaftanova, O.N.
机构：
来源：
Physics and chemistry of materials treatment | 1987年 / 21卷 / 01期
关键词：
CAST IRON - Wear Resisting - HEAT TREATMENT - Quenching - LASER BEAMS - Applications;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Optical and electron microscopy, x-ray diffraction analysis, microhardness measurements and wear resistance tests were used to examine the changes in the structure and properties of high-strength cast iron after the effect of the beam of a 2-4 kW CO//2 gas laser travelling at a speed of 1. 25-5 cm/sec. Formation of two types of layers with the zone of melting and the zone of quenching was observed. The heterogeneity of the structures in the zone of quenching causes differences in the microhardness in a relatively wide range. The highest wear resistance at a low degree of wear of the counterbody was recorded in the irradiated specimen in which the zone of quenching extended to the surface.
引用
收藏
页码：44 / 47
相关论文
共 50 条
  • [21] Melting of High-Quality Cast Iron.
    Caspers, Karl-Heinz
    1600, (73): : 25 - 26
  • [22] SELECTING THE METHOD OF NONDESTRUCTIVE INSPECTION OF THE MECHANICAL PROPERTIES OF HIGH-STRENGTH CAST IRON.
    Burtseva, V.A.
    Pravdin, L.S.
    Shcherbinin, V.E.
    Yakovlev, S.G.
    The Soviet journal of nondestructive testing, 1986, 22 (11): : 772 - 779
  • [23] Effect of Hot Working under Pressure on the Structure of High-Strength Cast Iron.
    Zamula, K.P.
    Petrichenko, A.M.
    Solntsev, L.A.
    Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya, 1977, (10): : 140 - 143
  • [24] MACHINING CAST IRON.
    Anon
    Casting Engineering, 1979, 11 (03): : 2 - 18
  • [25] Inoculation of Cast Iron.
    Henke, F.
    Giessereipraxis, 1980, (5-6): : 57 - 76
  • [26] Enamels for cast iron.
    Staley, HF
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1918, 1 (10) : 703 - 709
  • [27] MACHINING CAST IRON.
    Donaldson, E.G.
    Engineering (London), 1979, 219 (03):
  • [28] Inoculation of Cast Iron.
    Marincek, Borut
    Giesserei, 1975, 62 (26): : 692 - 694
  • [29] Synthetic cast iron.
    Mehrtens
    ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1920, 64 : 309 - 310
  • [30] ENGINEERING CAST IRON.
    Moore, William H.
    Casting engineering & foundry world, 1985, 16 (04): : 26 - 31
12345