SURACE TENSION OF MOLTEN STEEL.

被引：0
|
作者：
Tret'yakova, E.E.
Baum, B.A.
Tyagunov, G.V.
Klimenkov, E.A.
Tsepelev, V.S.
机构：
来源：
Russian metallurgy. Metally | 1986年 / 04期
关键词：
STEEL; -; Molten;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The temperature coefficient of surface tension of molten steel commonly has a positive sign. This suggests the breaking of surface-active associations between the atoms. The surface tension values ( sigma ) during heating and during their subsequent cooling coincide if heating does not proceed above the critical temperature t//c. When specimens are heated above t//c, their original structure does not recover during subsequent cooling.
引用
收藏
页码：25 / 28
相关论文
共 50 条
  • [21] Evaluation of interfacial tension between liquid steel and molten slag
    Tanaka, T
    Hara, S
    PROCEEDINGS OF THE 6TH INTERNATIONAL SYMPOSIUM ON MOLTEN SALT CHEMISTRY AND TECHNOLOGY, 2001, : 322 - 327
  • [22] IRON AND STEEL.
    McInnis, R.
    Canadian Mining Journal, 1983, 104 (02) : 98 - 99
  • [23] STRATEGIES FOR STEEL.
    McNeill, James
    SEAISI Quarterly (South East Asia Iron and Steel Institute), 1984, 13 (02): : 18 - 22
  • [24] STAINLESS STEEL.
    Anon
    CME. Chartered mechanical engineer, 1982, 29 (12): : 55 - 56
  • [25] Tinning of Steel.
    Siewert, Johannes
    1600, (94):
  • [26] Kiss of Steel.
    Ramsdell, Kristin
    LIBRARY JOURNAL, 2012, 137 (13) : 72 - 72
  • [27] Bessemer steel.
    Carpenter, HCH
    NATURE, 1924, 113 : 51 - 51
  • [28] Three-Phase ac Plasma Technology for Melting Scrap and Heating Molten Steel.
    Neuschuetz, D.
    Rossner, H.-O.
    Bebber, H.J.
    Heinen, K.-H.
    Elektrowaerme International, Edition B: Industrielle Elektrowaerme, 1987, 45 (02): : 76 - 81
  • [29] ROUGHNESS OF STEEL.
    Knott, J.F.
    Transactions of the Iron and Steel Institute of Japan, 1981, 21 (05) : 305 - 317
  • [30] KRAKATAU STEEL.
    Anon
    Steel Times, 1977, 205 (04): : 346 - 348
12345