Effect of ingredients on magnetic lifting property in bulk melt-textured YBCO

被引：0
|
作者：
General Research Inst for Nonferrous, Metals, Beijing, China [1 ]
机构：
来源：
J Rare Earth | / 1卷 / 63-66期
关键词：
Barium compounds - Copper compounds - Magnetic properties - Oxides - Yttrium compounds;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Bulk YBa2Cu3O7 samples were prepared by PMP method. Through adjusting ingredients and preparation procedures, a pellet with 3.5 cm in diameter and 0.9 cm in thickness was synthesized. A mass of 1.3 kg on a magnet can be levitated at about 1 mm height at 77 K. The XRD and SEM indicate that magnetic lifting property can be enhanced by the addition of Ag2O and Y2BaCuO5.
引用
收藏
相关论文
共 50 条
  • [41] High temperature deformation of Bridgman melt-textured YBCO
    Ullrich, M.
    Leenders, A.
    Krelaus, J.
    Kautschor, L.-O.
    Freyhardt, H.C.
    Schmidt, L.
    Sandiumenge, F.
    Obradors, X.
    Materials science & engineering. B, Solid-state materials for advanced technology, 1998, B53 (1-2): : 143 - 148
  • [42] Mechanical study on vortex entanglement in melt-textured YBCO
    Li, Z
    Zhu, JS
    Wu, XB
    Cai, CB
    Zhang, H
    Wang, YN
    PHYSICA C, 2000, 337 (1-4): : 281 - 284
  • [43] Effect of melt-processing temperature on the microstructure and the levitation force of YBCO melt-textured superconductors
    Yu, R
    Mora, J
    Vilalta, N
    Sandiumenge, F
    Gomis, V
    Pinol, S
    Obradors, X
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1997, 10 (08): : 583 - 589
  • [44] YBCO melt-textured growth seeded by superheating YBCO/MgO thin film
    Tang, CY
    Yao, X
    Hu, J
    Rao, QL
    Li, YR
    Tao, BW
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2005, 18 (06): : L31 - L34
  • [45] Structural and magnetic properties of silver doped melt-textured YBCO prepared in a solar furnace
    Godin, T
    Reich, S
    APPLIED SUPERCONDUCTIVITY, 1996, 4 (12) : 603 - 618
  • [46] Magnetization and resistance of melt-textured growth YBCO near Tc and at low magnetic fields
    Tiernan, W. M.
    Bingham, N. S.
    Combs, J. C.
    LOW TEMPERATURE PHYSICS, PTS A AND B, 2006, 850 : 459 - +
  • [47] Uranium fission fragment pinning centers in melt-textured YBCO
    Sawh, RP
    Weinstein, R
    Ren, Y
    Obot, V
    Weber, H
    PHYSICA C, 2000, 341 : 2441 - 2442
  • [48] Increased efficiency of batch-processed melt-textured YBCO
    Litzkendorf, D
    Habisreuther, T
    Bierlich, J
    Surzhenko, O
    Zeisberger, M
    Kracunovska, S
    Gawalek, W
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2005, 18 (02): : S206 - S208
  • [49] Levitation forces and mechanical properties of VGF melt-textured YBCO
    Ullrich, M
    Leenders, A
    Freyhardt, HC
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1997, 7 (02) : 1813 - 1816
  • [50] Dynamic scaling of ac susceptibility in melt-textured YBCO superconductors
    Liu, SL
    Wu, GJ
    Tan, HJ
    Xu, XB
    Shao, HM
    Cai, YM
    Shen, SL
    Jin, XC
    PHYSICS LETTERS A, 2006, 353 (2-3) : 241 - 244
12345