Effect of ingredients on magnetic lifting property in bulk melt-textured YBCO

被引：0
|
作者：
General Research Inst for Nonferrous, Metals, Beijing, China [1 ]
机构：
来源：
J Rare Earth | / 1卷 / 63-66期
关键词：
Barium compounds - Copper compounds - Magnetic properties - Oxides - Yttrium compounds;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Bulk YBa2Cu3O7 samples were prepared by PMP method. Through adjusting ingredients and preparation procedures, a pellet with 3.5 cm in diameter and 0.9 cm in thickness was synthesized. A mass of 1.3 kg on a magnet can be levitated at about 1 mm height at 77 K. The XRD and SEM indicate that magnetic lifting property can be enhanced by the addition of Ag2O and Y2BaCuO5.
引用
收藏
相关论文
共 50 条
  • [1] Effect　of　Ingredients　on　Magnetic　Lifting　Property　in　Bulk　Melt－Textured　YBCO
    付雪奎
    肖玲
    任洪涛
    Journal of Rare Earths, 1995, (01) : 63 - 66
  • [2] EFFECT OF Y2BACUO5 PHASE CONTENT ON MAGNETIC PROPERTY IN BULK MELT-TEXTURED YBCO
    FU, XK
    XIAO, L
    REN, HT
    JOURNAL OF RARE EARTHS, 1995, 13 (02) : 137 - 139
  • [3] Effect　of　Y2BaCuO5　Phase　Content　on　Magnetic　Property　in　Bulk　Melt－textured　YBCO
    付雪奎
    肖玲
    任洪涛
    JOURNAL OF RARE EARTHS, 1995, (02) : 137 - 139
  • [4] Effect of Y2BaCuO5 phase content on magnetic property in bulk melt-textured YBCO
    General Research Inst for, Non-ferrous Metals, Beijing, China
    J Rare Earth, 2 (137-139):
  • [5] Effect of mesoscopic inhomogeneities on the critical current of bulk melt-textured YBCO
    Uspenskaya, LS
    Naumenko, IG
    Emelchenko, GA
    Boguslavskii, YB
    Zver'kov, SA
    Yakimov, EB
    Litzkendorf, D
    Gawalek, W
    Caplin, AD
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 390 (02): : 127 - 133
  • [6] Hysteresis electrical motors with bulk melt-textured YBCO
    Kovalev, L.K.
    Ilushin, K.V.
    Penkin, V.T.
    Kovalev, K.L.
    Semenikhin, V.S.
    Poltavets, V.N.
    Larionoff, A.E.
    Gawalek, W.
    Habisreuther, T.
    Strasser, T.
    Shikov, A.K.
    Kazakov, E.G.
    Alexandrov, V.V.
    Materials science & engineering. B, Solid-state materials for advanced technology, 1998, B53 (1-2): : 216 - 219
  • [7] Oxygenation and cracking in melt-textured YBCO bulk superconductors
    Kracunovska, S
    Diko, P
    Litzkendorf, D
    Habisreuther, T
    Bierlich, J
    Gawalek, W
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2005, 18 (02): : S142 - S148
  • [8] Hysteresis electrical motors with bulk melt-textured YBCO
    Kovalev, LK
    Ilushin, KV
    Penkin, VT
    Kovalev, KL
    Semenikhin, VS
    Poltavets, VN
    Larionoff, AE
    Gawalek, W
    Habisreuther, T
    Strasser, T
    Shikov, AK
    Kazakov, EG
    Alexandrov, VV
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1998, 53 (1-2): : 216 - 219
  • [9] Developing melt-textured YBCO
    T. Habisreuther
    M. Zeisberger
    D. Litzkendorf
    O. Surzhenko
    W. Gawalek
    JOM, 2000, 52 : 26 - 28
  • [10] Developing melt-textured YBCO
    Habisreuther, T
    Zeisberger, M
    Litzkendorf, D
    Surzhenko, O
    Gawalek, W
    JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 2000, 52 (06): : 26 - 28
12345