PREVENTION OF THE FORMATION OF LONGITUDINAL FACIAL CRACKS ON CONTINUOUSLY CAST SLABS BY IMPROVING MOLD POWDER AND MOLD OSCILLATION.

被引：0

|

作者：

Sakuraya, Toshikazu

Emi, Toshihiko

Imai, Takuo

Emoto, Kanji

Kodama, Masanori

机构：

来源：

Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan | 1981年 / 67卷 / 08期

关键词：

Compendex;

D O I：

10.2355/tetsutohagane1955.67.8_1220

中图分类号：

学科分类号：

摘要：

STEEL

引用

收藏

页码：1220 / 1228

相关论文

共 50 条

[21] MOLD BEHAVIOR AND ITS INFLUENCE ON QUALITY IN THE CONTINUOUS-CASTING OF STEEL SLABS .2. MOLD HEAT-TRANSFER, MOLD FLUX BEHAVIOR, FORMATION OF OSCILLATION MARKS, LONGITUDINAL OFF-CORNER DEPRESSIONS, AND SUBSURFACE CRACKS
MAHAPATRA, RB
BRIMACOMBE, JK
SAMARASEKERA, IV
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1991, 22 (06): : 875 - 888
[22] OBSERVATION OF LIQUID-SOLID INTERFACE IN CONTINUOUSLY CAST STEEL SLABS BY LEAD ADDITIONS TO MOLD
KAWAWA, T
KITAGAWA, T
MURAKAMI, K
CANADIAN METALLURGICAL QUARTERLY, 1976, 15 (02) : 129 - 137
[23] Prediction and analysis on formation of internal cracks in continuously cast slabs by mathematical models
Han, ZQ
Cai, KK
Liu, BC
ISIJ INTERNATIONAL, 2001, 41 (12) : 1473 - 1480
[24] Measurement of critical strain for the formation of transverse cracks on continuously cast steel slabs
Suzuki, M
Hayashi, H
Shibata, H
Emi, T
THERMEC '97 - INTERNATIONAL CONFERENCE ON THERMOMECHANICAL PROCESSING OF STEELS AND OTHER MATERIALS, VOLS I-II, 1997, : 2255 - 2261
[25] Transverse Surface Cracks in Continuously Cast Steel Slabs, Oscillation Marks and Austenite Grain Size
Dippenaar, Rian
THERMEC 2009, PTS 1-4, 2010, 638-642 : 3603 - 3609
[26] COMPARATIVE CORROSION TESTS ON STEEL PLATES ROLLED FROM CONTINUOUSLY CAST SLABS AND ROLLED FROM MOLD CAST INGOTS
JOSEFSSON, A
LOUNAMAA, K
CORROSION, 1981, 37 (05) : 279 - 284
[27] COMPARATIVE CORROSION TESTS ON STEEL PLATES ROLLED FROM CONTINUOUSLY CAST SLABS AND ROLLED FROM MOLD CAST INGOTS
WRANGLEN, G
CORROSION, 1982, 38 (01) : 59 - 60
[28] FACTORS AFFECTING THE FORMATION OF SHELL AND LONGITUDINAL CRACKS IN MOLD DURING HIGH-SPEED CONTINUOUS-CASTING OF SLABS
NAKATO, H
OZAWA, M
KINOSHITA, K
HABU, Y
EMI, T
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 24 (11) : 957 - 965
[29] Finite element analysis on stress development of soldifying shell in the mold of continuously cast steel thin slabs
Ying Yong Li Xue Xue Bao/Chinese Journal of Applied Mechanics, 1994, 11 (02):
[30] Improvement of Castability and Surface Quality of Continuously Cast TWIP Slabs by Molten Mold Flux Feeding Technology
Jung-Wook Cho
Shin Yoo
Min-Seok Park
Joong-Kil Park
Ki-Hyeon Moon
Metallurgical and Materials Transactions B, 2017, 48 : 187 - 196

← 1 2 3 4 5 →