Synthesis of cubic Cs2FeSi5O12 powder in Ar atmosphere and its thermal expansion property

被引：0
|
作者：
Yanase, Ikuo [1 ,3 ]
Kobayashi, Hidehiko [1 ]
Mitamura, Takashi [2 ]
机构：
[1] Department of Applied Chemistry, Faculty of Engineering, Saitama University, 255, Shimoohkubo, Urawa-shi, Saitama 338-8570, Japan
[2] Graduate School, Saitama Institute of Technology, 1690, Fusaiji, Okabe-machi, Ohsato-gun, Saitama 369-0293, Japan
[3] Natl. Inst. for Res. in Inorg. Mat., 1-1, Namiki, Tsukuba-shi, Ibaraki 305-0044, Japan
来源：
Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan | 2000年 / 108卷 / 1259期
关键词：
Amorphous materials - Argon - Cesium compounds - High temperature properties - Iron oxides - Silica - Synthesis (chemical) - Thermal expansion - X ray diffraction analysis;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Cubic Cs2FeSi5O12 powder with the space group Ia-3d was synthesized by heating the powder mixture of Cs2CO3&middot2H2O, Fe3O4 and amorphous SiO2 with the molar ratio of Cs/Fe = 2 and Si/Fe = 5 at 1273 K for 20 h under Ar gas flow. The thermal expansion property of cubic Cs2FeSi5O12 powder was investigated in the temperature range from 298 to 1273 K using high-temperature X-ray diffraction. The thermal expansion rate of cubic Cs2FeSi5O12 was lower than that of cubic CsFeSi2O6. Consequently, increasing the molar ratio of Si/Fe was effective for decreasing the thermal expansion rate of Cs-Fe-leucite compounds. Cubic Cs2FeSi5O12 showed a lower thermal expansion with the mean linear thermal expansion coefficient of 1.75×10-6 K-1 in the range from 573 to 1273 K.
引用
收藏
页码：677 / 680
相关论文
共 50 条
  • [31] Synthesis of Zr2WP2O12/ZrO2 Composites with Adjustable Thermal Expansion
    Zhang, Zhiping
    Sun, Weikang
    Liu, Hongfei
    Xie, Guanhua
    Chen, Xiaobing
    Zeng, Xianghua
    FRONTIERS IN CHEMISTRY, 2017, 5
  • [32] Low Temperature Synthesis of Negative Thermal Expansion Y2W3O12
    Satyabati Das
    Siddhartha Das
    Karabi Das
    Journal of Materials Engineering and Performance, 2013, 22 : 3357 - 3363
  • [33] Low Temperature Synthesis of Negative Thermal Expansion Y2W3O12
    Das, Satyabati
    Das, Siddhartha
    Das, Karabi
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (11) : 3357 - 3363
  • [34] Synthesis of Negative Thermal Expansion Sc2W3O12 Thin Film
    Zhang Zhi-Ping
    Liu Hong-Fei
    Pan Kun-Min
    Chen Xiao-Bing
    Zeng Xiang-Hua
    JOURNAL OF INORGANIC MATERIALS, 2015, 30 (12) : 1278 - 1282
  • [35] Preparation and thermal expansion of Fe2-xYxW3O12 powder by citrate sol-gel process
    Zhang, Haijun
    Zhang, Qing
    Du, Honglin
    Jia, Quanli
    CHEMICAL ENGINEERING COMMUNICATIONS, 2008, 195 (03) : 243 - 255
  • [36] Synthesis of Sc2W3O12/ZrO2 composites with controllable thermal expansion
    Cheng, X. (xncheng@ujs.edu.cn), 2012, Beijing University of Aeronautics and Astronautics (BUAA) (29):
  • [37] Synthesis and thermal expansion properties of Y2-xLaxMo3O12 (x=0, 0.5, 2)
    Liu, Hongfei
    Wang, Xiaocen
    Zhang, Zhiping
    Chen, Xiaobing
    CERAMICS INTERNATIONAL, 2012, 38 (08) : 6349 - 6352
  • [38] THERMAL-EXPANSION ANISOTROPY GRAIN-SIZE MECHANICAL PROPERTY EFFECTS IN MGTI2O5
    KUSZYK, JA
    BRADT, RC
    AMERICAN CERAMIC SOCIETY BULLETIN, 1973, 52 (04): : 340 - 340
  • [39] Effects of doping Fe cations on crystal structure and thermal expansion property of Yb2Mo3O12
    Cheng, Ying-Zhi
    Sun, Xiu-Yu
    Xiao, Xiao-Ling
    Liu, Xiang-Feng
    Xue, Li
    Hu, Zhong-Bo
    CHINESE CHEMICAL LETTERS, 2017, 28 (07) : 1600 - 1606
  • [40] Effects of doping Fe cations on crystal structure and thermal expansion property of Yb2Mo3O12
    Ying-Zhi Cheng
    Xiu-Yu Sun
    Xiao-Ling Xiao
    Xiang-Feng Liu
    Li Xue
    Zhong-Bo Hu
    Chinese Chemical Letters, 2017, 28 (07) : 1600 - 1606
12345