Effect of aging on mixed-mode I/III fracture toughness of 2034 aluminum alloys

被引：0
|
作者：
Washington State Univ, Pullman, United States [1 ]
机构：
来源：
Acta Mater | / 3卷 / 1047-1054期
基金：
美国国家科学基金会;
关键词：
Aging of materials - Cracks - Deformation - Fracture - Fracture toughness - Loads (forces) - Manganese - Metallographic microstructure - Tempering;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of aging on the mixed-mode I/III fracture toughness was evaluated for two 2034 Al type alloys with different Mn content. The effect of aging was found to be significantly different in the two alloys. Alloy 1 which had < 0.1 wt% Mn exhibited a significant reduction in fracture toughness with increasing mode III loading contribution. In this alloy, increasing aging time resulted in less reduction of fracture toughness with increasing mode III loading contribution. On the other hand, alloy 2 which had 1.08 wt% Mn exhibited a marginal effect of mixed-mode loading on fracture toughness. In this alloy increasing aging time did not result in a significant change in the mixed-mode fracture behavior. The results are discussed in light of the microstructures, fracture mechanisms and deformation field ahead of the crack tip under mixed-mode loading.
引用
收藏
相关论文
共 50 条
  • [41] Effect of T-stress on the initial fracture toughness of concrete under I/II mixed-mode loading
    Zhao, Yanhua
    Dong, Wei
    Xu, Bohan
    Liu, Jin
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2018, 96 : 699 - 706
  • [42] Mixed-mode interfacial fracture toughness for thermal barrier coating
    Arai, M.
    Kajima, Y.
    Kishimoto, K.
    ENGINEERING FRACTURE MECHANICS, 2007, 74 (13) : 2055 - 2069
  • [43] Fracture toughness of mixed-mode anticracks in highly porous materials
    Adam, Valentin
    Bergfeld, Bastian
    Weissgraeber, Philipp
    van Herwijnen, Alec
    Rosendahl, Philipp L.
    NATURE COMMUNICATIONS, 2024, 15 (01)
  • [44] Effect of double-aging on the fracture toughness of 2090 and 2091 aluminum alloys
    Yamaguchi Univ, Yamaguchi, Japan
    Keikinzoku J Jpn Inst Light Met, 11 (660-665):
  • [45] Mode I, mode II, and mixed-mode I/II interlaminar fracture toughness of GFRP influenced by fiber surface treatment
    Rikards, R
    Buchholz, FG
    Bledzki, AK
    Wacker, G
    Korjakin, A
    MECHANICS OF COMPOSITE MATERIALS, 1996, 32 (05) : 439 - 462
  • [46] MIXED-MODE FRACTURE-ANALYSIS AND TOUGHNESS OF ADHESIVE JOINTS
    PANG, HLJ
    ENGINEERING FRACTURE MECHANICS, 1995, 51 (04) : 575 - +
  • [47] Loading Rate Effects for Flaws Undergoing Mixed-Mode I/III Fracture
    Fahem, A.
    Kidane, A.
    Sutton, M.
    EXPERIMENTAL MECHANICS, 2021, 61 (08) : 1291 - 1307
  • [48] Mixed-mode I plus III interlaminar fracture of carbon/epoxy laminates
    Pereira, A. B.
    de Morais, A. B.
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2009, 40 (04) : 518 - 523
  • [49] Loading Rate Effects for Flaws Undergoing Mixed-Mode I/III Fracture
    A. Fahem
    A. Kidane
    M. Sutton
    Experimental Mechanics, 2021, 61 : 1291 - 1307
  • [50] Effect of Aging on Impact Toughness and Fracture Behavior of Three Wrought Aluminum Alloys
    Gong, BaiShan
    Zhang, ZhenJun
    Duan, QiQiang
    Hou, JiaPeng
    Li, RongHua
    Wang, XueGang
    Liu, HanZhong
    Cong, FuGuan
    Purcek, Gencay
    Zhang, ZheFeng
    ADVANCED ENGINEERING MATERIALS, 2023, 25 (14)
12345