REDISTRIBUTION OF CARBON AND OXYGEN IN SEMICRYSTALLINE MOLYBDENUM DURING ANNEALING.

被引：0
|
作者：
Ban'kovskii, O.I. [1 ]
Ivashchenko, Yu.N. [1 ]
Krainikov, A.V. [1 ]
Pechkovskii, E.P. [1 ]
Polishchuk, E.P. [1 ]
机构：
[1] Acad of Sciences of the UkrSSr, USSR, Acad of Sciences of the UkrSSr, USSR
来源：
Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka | 1986年 / 28卷 / 11-12期
关键词：
HEAT TREATMENT - Annealing - MOLYBDENUM METALLOGRAPHY - Segregation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
An increase in the annealing temperature of deformed molybdenum containing 0. 011% of interstitial elements in the 1150-1550 degree C interval effects an increase in the amount of carbon and oxygen atoms on the grain boundaries as a result of segregation. After annealing above 1350 degree C, the outflow of interstitial elements onto the boundaries takes place incompletely, as a result of which a supersaturated solid solution is formed. Subsequent annealing at 1150 degree C for 4 h leads to an additional increase in oxygen content and the formation of molybdenum carbide particles on the boundaries; this causes a small decrease in strength and a decrease in plasticity.
引用
收藏
页码：891 / 894
相关论文
共 50 条
  • [41] DEPENDENCE OF OXYGEN REDISTRIBUTION ON TITANIUM FILM THICKNESS DURING TITANIUM SILICIDE FORMATION BY RAPID THERMAL ANNEALING
    KANG, SW
    CHUN, JS
    PARK, SC
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1989, 7 (06): : 3246 - 3250
  • [42] CHEMISORPTION OF CARBON AND OXYGEN ON MOLYBDENUM SURFACES
    TOUBOUL, JP
    AILLOUD, P
    MINEL, L
    LANGERON, JP
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES SERIE C, 1969, 269 (02): : 116 - &
  • [43] SOLUBILITY OF CARBON AND OXYGEN IN MOLYBDENUM - DISCUSSION
    GOKCEN, NA
    FEW, WE
    MANNING, GK
    TRANSACTIONS OF THE AMERICAN INSTITUTE OF MINING AND METALLURGICAL ENGINEERS, 1953, 197 (05): : 746 - 747
  • [44] The redistribution of carbon and oxygen in crystallizing white dwarfs
    Mochkovitch, R
    Isern, J
    Hernanz, M
    GarciaBerro, E
    WHITE DWARFS, 1997, 214 : 19 - 25
  • [45] VOID FORMATION DURING ANNEALING OF IRRADIATED MOLYBDENUM
    EVANS, JH
    EYRE, BL
    MAHAJAN, S
    PHILOSOPHICAL MAGAZINE, 1972, 26 (04): : 813 - &
  • [46] GROWTH OF SUBGRAINS IN DEFORMED MOLYBDENUM DURING ANNEALING
    DUBOVITSKAYA, NV
    LARIKOV, LN
    PHYSICS OF METALS AND METALLOGRAPHY, 1971, 32 (05): : 193 - 198
  • [47] DOPANT REDISTRIBUTION DURING ANNEALING OF AMORPHIZED SI(111)
    TURAN, R
    FINSTAD, TG
    PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1991, 63 (03): : 519 - 525
  • [48] IRON REDISTRIBUTION PROCESSES IN ALUMINUM DURING RECRYSTALLIZATION ANNEALING
    NECHAYEV, YS
    KRUPIN, YA
    MEZHENNYY, YA
    PUSTOV, YA
    RASTORGUYEV, LN
    FIZIKA METALLOV I METALLOVEDENIE, 1984, 58 (05): : 958 - 967
  • [49] Arsenic Desorption and Interaction Reactions in the Au-GaAs System during Thermal Annealing.
    Bryansteva, T.A.
    Dvoryankina, G.G.
    Lebedeva, Z.M.
    Ormont, A.B.
    Petrov, A.G.
    Yunevich, E.O.
    Neorganiceskie materialy, 1986, 22 (06): : 889 - 892
  • [50] Change of state for oxygen contaminant and reaction of components during vacuum annealing of a mixture of molybdenum and boron powders
    Bloshenko, V.N.
    Bokii, V.A.
    Moravskaya, T.M.
    Shul'ga, Yu.M.
    Combustion, Explosion and Shock Waves, 1988, 23 : 226 - 229
12345