INFLUENCE OF THE ORIGINAL MICROPOROSITY ON THE LIFE OF ALUMINIUM.

被引：0
|
作者：
Betekhtin, V.I.
Petrov, A.I.
Kadomtsev, A.G.
机构：
来源：
Physics of Metals and Metallography | 1975年 / 40卷 / 04期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
These results show that the original (before testing) concentration of microdiscontinuities exerts an influence on the time-to-rupture, which decreases as the latter grows. Analysis of the processes controlling the rate of failure (time-to-rupture) would generally have to take account of the original microporosity although, it does not have a very great influence on the strength.
引用
收藏
页码：202 / 204
相关论文
共 50 条
  • [41] HARD ANODISING IMPROVES ALUMINIUM.
    Atkinson, Michael
    Engineering (London), 1983, 223 (07): : 528 - 530
  • [42] Mineral chemistry - On the corrosion of aluminium.
    Calvet, J
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES, 1929, 188 : 1111 - 1114
  • [43] Calalytic appearances in the decomposition of aluminium.
    Centnerszwer, M
    ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE--STOCHIOMETRIE UND VERWANDTSCHAFTSLEHRE, 1928, 131 (3/4): : 214 - 225
  • [44] On knowledge of anodic behaviour of aluminium.
    Muller, WJ
    Konopicky, K
    ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE--STOCHIOMETRIE UND VERWANDTSCHAFTSLEHRE, 1929, 141 (5/6): : 343 - 377
  • [45] Information on the anodic behaviour of aluminium.
    Guntherschulze, A
    ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE-ABTEILUNG A-CHEMISCHE THERMODYNAMIK KINETIK ELEKTROCHEMIE EIGENSCHAFTSLEHRE, 1929, 143 (01): : 62 - 68
  • [46] Review of anodic behaviour of aluminium.
    Guntherschulze, A
    Muller, WJ
    Konopicky, K
    ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE-ABTEILUNG A-CHEMISCHE THERMODYNAMIK KINETIK ELEKTROCHEMIE EIGENSCHAFTSLEHRE, 1929, 145 (3/4): : 256 - 256
  • [47] A note on the spectra of silicon and aluminium.
    McQuarrie, WC
    PHILOSOPHICAL MAGAZINE, 1925, 50 (298): : 819 - 821
  • [48] Effect of chloride of anhydrous aluminium.
    Baud, E
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES, 1900, 130 : 1319 - 1322
  • [49] INFLUENCE OF RESIDUAL AIR PRESSURE ON THE COEFFICIENT OF SURFACE DIFFUSION IN COPPER AND ALUMINIUM.
    Yushin, V.D.
    Logvinov, A.N.
    Chempinskiy, L.A.
    Shakhnistov, V.M.
    Physics of Metals and Metallography, 1976, 41 (03): : 196 - 199
  • [50] ROLL CLADDING OF COPPER ON ALUMINIUM.
    Bhattacharya, J.
    Ghose, B.N.
    Banerjee, S.K.
    Sheet Metal Industries, 1983, 60 (05): : 300 - 302
12345