Tests confirm polyethylene pipe for high-pressure oil, gas service

被引：0
|
作者：
Anon
机构：
来源：
IEEE Multimedia | / 3卷 / 03期
关键词：
Carbon steel - Crack propagation - Crude petroleum - Fiber reinforced plastics - Fracture toughness - High density polyethylenes - High pressure effects - Mechanical testing - Oil fields - Thermoplastics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Shell International, The Hague, has conducted mechanical-resistance tests on reinforced high-density polyethylene (HDPE) pipe. Results confirmed the pipe's service pressure of up to 150 bar (2,175 psi) in temperatures of -30°C to 30°C. The pressure ranges vary with the number of reinforcement levels. At greater than 30°C, the service pressure must be reduced by 10 bar for each 10°C increase.
引用
收藏
页码：52 / 55
相关论文
共 50 条
  • [31] An estimation of the high-pressure pipe residual life
    Jovicic, G.
    Nikolic, R.
    Zivkovic, M.
    Milavanovic, D.
    Jovicic, N.
    Maksimovic, S.
    Djordjevic, J.
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2013, 13 (01) : 36 - 44
  • [32] HIGH-PRESSURE GAS QUENCHING
    CONYBEAR, JG
    ADVANCED MATERIALS & PROCESSES, 1993, 143 (02): : 20 - 21
  • [33] High-pressure gas hydrates
    Loveday, J. S.
    Nelmes, R. J.
    PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2008, 10 (07) : 937 - 950
  • [34] High-pressure gas lighting
    不详
    JOURNAL OF INDUSTRIAL AND ENGINEERING CHEMISTRY-US, 1912, 4 : 915 - 915
  • [35] High-pressure gas hydrates
    Loveday, J. S.
    Nelmes, R. J.
    Maynard, H. E.
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 2007, 63 : S217 - S217
  • [36] DSC Tests on high-pressure cell
    Research & Development (Barrington, Illinois), 1994, 36 (11):
  • [37] ULTRASONIC STUDY OF HIGH-PRESSURE PHASE IN POLYETHYLENE
    NAGATA, K
    TAGASHIRA, K
    TAKI, S
    TAKEMURA, T
    JAPANESE JOURNAL OF APPLIED PHYSICS, 1980, 19 (05) : 985 - 990
  • [38] High-pressure pyrolysis and its mechanism of polyethylene
    Gu J.
    Cheng L.-L.
    Wang Y.-Z.
    Zhang Y.-X.
    Yuan H.-R.
    Yuan, Hao-Ran (yuanhr@ms.giec.ac.cn), 1600, Science Press (49): : 395 - 406
  • [39] NATURE OF DISORDER IN THE HIGH-PRESSURE PHASE OF POLYETHYLENE
    YAMAMOTO, T
    JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1979, B16 (04): : 487 - 509
  • [40] DEFECT STRUCTURES IN HIGH-PRESSURE CRYSTALLIZED POLYETHYLENE
    SCHAPER, A
    ACTA POLYMERICA, 1986, 37 (07) : 471 - 474
12345