DEFORMATION OF TITANIUM CARBIDE AT HIGH TEMPERATURES.

被引：0

作者：

Chermant, Jean Louis

Leclerc, Gilles

Mordike, Barry L.

机构：

来源：

Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques | 1980年 / 71卷 / 07期

关键词：

D O I：

暂无

中图分类号：

O6 [化学]; TQ [化学工业];

学科分类号：

0703 ; 0817 ;

摘要：

The deformation of polycrystalline titanium carbide was investigated in compression and in three-point bending over the temperature range from 1673 to 2273 K. At moderate temperatures ( less than 2000 K), dislocation movement is controlled by the diffusion of carbon with an activation energy for deformation of 5 eV. At higher temperatures the deformation is controlled by the diffusion of vacancies, with an activation energy of 7 eV.

引用

页码：465 / 469

共 50 条

[31] A thermostat for moderate and high temperatures.
Haughton, JL
Hanson, D
JOURNAL OF THE INSTITUTE OF METALS, 1915, 14 : 145 - 151
[32] Nernst and the chemistry of high temperatures.
von Wartenberg, H
NATURWISSENSCHAFTEN, 1943, 31 : 307 - 309
[33] Catalytic combustion at high temperatures.
Davies, W.
PHILOSOPHICAL MAGAZINE, 1935, 19 (124-30) : 309 - +
[34] The expansion of metals at high temperatures.
Uffelmann, FL
PHILOSOPHICAL MAGAZINE, 1930, 10 (65): : 633 - 659
[35] Catalytic combustion at high temperatures.
Davies, W
PHILOSOPHICAL MAGAZINE, 1935, 19 (126): : 309 - +
[36] The disintegration of metals at high temperatures.
Roberts, JHT
NATURE, 1912, 89 : 660 - 660
[37] The friction of lubricants at high temperatures.
Kapff, S
ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1901, 45 : 343 - 345
[38] OXIDATION OF COBALT AT HIGH TEMPERATURES.
Mrowec, S.
Przybylski, K.
1600, (14):
[39] Oxidation of Some Titanium Alloys in Air at Elevated Temperatures.
Godlewska, E.
Mitoraj, M.
Jajko, B.
HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 967 - 974
[40] Phenomena Occurring During Deformation of BA1032 Aluminum Bronze at High Temperatures.
Gronostajski, Jerzy
Ziemba, Henryk
Archiwum Hutnictwa, 1979, 24 (01): : 67 - 78

← 1 2 3 4 5 →