Biaxial stress corrosion cracking of 316L stainless steel in MgCl2 (44%) at 154°C

被引：0
|
作者：
Farre, M.T.
Andrieu, E.
Pilvin, P.
Vancon, D.
机构：
[1] Ctr. des Mat. Pierre-Marie Fourt, Ecl. Natl. Sup. des Mines de Paris, BP87, 91003 Evry Cedex, France
[2] Ecl. Natl. Sup. de Chim. de Toulouse, 118 route de Narbonne, 31077 Toulouse Cedex, France
[3] Ecole Centrale de Paris, LMSS-Matériaux, Grande Voie des Vignes, 92295 Châtenay-Malabry Cedex, France
[4] Electricité de France, E.M.A, Les Renardières, route de Sens, 77250 Moret sur Loing, France
[5] Centre des Matériaux, E.N.S.M.P., B.P.87, 91003 Evry Cedex, France
来源：
Annales de Chimie: Science des Materiaux | / 24卷 / 4-5期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：313 / 319
相关论文
共 50 条
  • [11] Stress corrosion cracking of long term ageing-treated 316 stainless steel in boiling 42% MgCl2 solution
    Vanderbilt Univ, Nashville, United States
    J Mater Sci Lett, 3 (244-247):
  • [12] Stress corrosion cracking of long term ageing-treated 316 stainless steel in boiling 42% MgCl2 solution
    Li, DL
    Mao, X
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1997, 16 (03) : 244 - 247
  • [13] A research on the corrosion and stress corrosion cracking susceptibility of 316L stainless steel exposed to supercritical water
    Guo, Xianglong
    Chen, Kai
    Gao, Wenhua
    Shen, Zhao
    Lai, Ping
    Zhang, Lefu
    CORROSION SCIENCE, 2017, 127 : 157 - 167
  • [14] Stress corrosion cracking behavior of warm forged 316L stainless steel at different orientations
    Du, Donghai
    Wang, Jiamei
    Chen, Kai
    Zhang, Lefu
    JOURNAL OF NUCLEAR MATERIALS, 2019, 522 : 220 - 225
  • [15] Effect of surface nanocrystallization induced by mechanical grinding treatment on stress corrosion cracking behavior of 316 L austenitic stainless steel in boiling MgCl2 solution
    Yang, Chongwen
    Jiang, Xinli
    Zhang, Wenqian
    Wang, Xuelin
    MATERIALS CHARACTERIZATION, 2024, 218
  • [16] Stress corrosion cracking of austenitic stainless steel single and polycrystals in MgCl2 : an attempt at improving the resistance
    Paret, A.
    Magnin, T.
    Annales de Chimie: Science des Materiaux, 24 (4-5): : 253 - 262
  • [17] STRESS-CORROSION CRACKING OF CRNI MARTENSITIC STAINLESS-STEEL IN CONCENTRATED MGCL2 SOLUTIONS
    YOSHINO, Y
    CORROSION, 1986, 42 (10) : 592 - 600
  • [18] STRESS-CORROSION CRACKING BEHAVIOR OF DUPLEX STAINLESS-STEEL WELDMENTS IN BOILING MGCL2
    SHERMAN, DH
    DUQUETTE, DJ
    SAVAGE, WF
    CORROSION, 1975, 31 (10) : 376 - 380
  • [19] The role of hydrogen in stress corrosion cracking of 310 austenitic stainless steel in a boiling MgCl2 solution
    Wang, W. W.
    Su, Y. J.
    Yan, Y.
    Li, J. X.
    Qiao, L. J.
    Chu, W. Y.
    Wang, X. K.
    Xing, Y.
    CORROSION SCIENCE, 2012, 60 : 275 - 279
  • [20] Corrosion fatigue cracking of AISI 316L stainless steel screen mesh
    Kaewkumsai, S.
    Khonraeng, W.
    Chainpairote, A.
    ENGINEERING FAILURE ANALYSIS, 2010, 17 (04) : 857 - 863
12345