Effect of Stress Concentration on Fatigue Resistance of Refractory Nickel Alloys under Asymmetric Multicycle Loading. Communication 1.

被引：0

作者：

Sinaiskii, B.N.

机构：

来源：

Problemy Prochnosti | 1984年 / 03期

关键词：

FATIGUE OF MATERIALS - Stresses;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Results are given for experimental studies on fatigue resistance of refractory nickel alloys (deformable EP109 and casting ZhS6U) obtained for smooth specimens and specimens with a round notch at an elevated temperature and with different stress ratios. The effect of stress concentration on fatigue resistance is shown to depend on the alloy type and amplitude coefficient, the experimental time exerting a slight influence.

引用

共 40 条

[21] Fatigue damage accumulation in aluminium and titanium alloys subjected to block program loading under conditions of stress concentration and fretting
Troshchenko, VT
Dragan, VI
Semenyuk, SM
INTERNATIONAL JOURNAL OF FATIGUE, 1999, 21 (03) : 271 - 279
[22] Variation of creep stresses and structure of welds from PT-3V titanium alloys under the action of cyclic loading. Communication 1
Inst Problem Prochnosti AN Ukrainy, Kiev, Ukraine
Probl Prochn, 4 (27-33):
[23] REGULARITIES OF STRAIN AND FAILURE IN THE METAL OF WELDED JOINTS OF CONSTRUCTION STEEL AT ELEVATED TEMPERATURES UNDER THE CONDITIONS OF STATIC AND LOW-CYCLE LOADING. COMMUNICATION 1. STRAIN RESISTANCE.
Khanukhov, Kh.M.
Problemy Prochnosti, 1987, (09): : 28 - 32
[24] Application of High Frequency Loading Methods for Accelerated Determination of the Effect of Technological, Structural and Operating Factors on Fatigue Failure Resistance. Communication 1.
Kuz'menko, V.A.
Matokhnyuk, L.E.
Voinalovich, A.V.
Rodionov, Yu.V.
1600,
[25] FATIGUE STRENGTH OF EXTERNAL AND INTERNAL STEEL SCREW THREADS UNDER AXIAL LOADING. (STANDARD FORMS NOT GREATER THAN 1. 0 INCH DIAMETER).
Anon
1984,
[26] Effect of Creep and Cyclic Loading on Pulsating Fatigue Behavior for Various Ti Alloys under Stress Ratio R=0
Nagatani, Gen-ichiro
Kitazawa, Rumi
Yoshida, Makoto
Horibe, Susumu
JOURNAL OF THE JAPAN INSTITUTE OF METALS AND MATERIALS, 2013, 77 (10) : 455 - 460
[27] Effect of creep and cyclic loading on pulsating fatigue behavior for various ti alloys under stress ratio R = 0
Nagatani, Gen-Ichiro
Kitazawa, Rumi
Yoshida, Makoto
Horibe, Susumu
Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, 2013, 77 (10): : 455 - 460
[28] Effect of Stress Relaxation and Creep on Life of 12Cr1MoV Steel Under Low-Cycle Loading.
Zelenskii, V.G.
Sevryugin, V.V.
1600,
[29] The effect of MWCNT concentration on the electrical resistance change characteristic of glass/fiber epoxy composites under low cycle fatigue loading
Turan, Fatih
MATERIALS TESTING, 2025, 67 (01) : 1 - 16
[30] Deformation Relief of the Surface as a Characteristic of Fatigue Damage of Clad Aluminum Alloys. Part 1. Deformation Relief Evolution Under Cyclic Loading
Ignatovich, S. R.
Karuskevich, M. V.
Yutskevich, S. S.
STRENGTH OF MATERIALS, 2020, 52 (05) : 707 - 714

← 1 2 3 4 →