MORPHOLOGY AND CHARACTERIZATION OF POLYACETYLENE FILMS SYNTHESIZED IN A LIQUID CRYSTAL SOLVENT.

被引：0
|
作者：
Araya, K. [1 ]
Mukoh, A. [1 ]
Narahara, T. [1 ]
Akagi, K. [1 ]
Shirakawa, H. [1 ]
机构：
[1] Hitachi Ltd, Kokubunji, Jpn, Hitachi Ltd, Kokubunji, Jpn
来源：
Synthetic Metals | 1986年 / 17卷 / 1-3期
关键词：
CRYSTALS; LIQUID - Nematic - POLYMERIZATION - POLYMERS - Electric Conductivity - SOLVENTS;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The synthesis of oriented polyacetylene films was investigated by using a nematic liquid crystal as a polymerization solvent. As a result, when polymerization was carried out on a quiesent surface of the nematic catalyst solution, partially oriented polyacetylene films were obtained. On the other hand, in the polymerization under a flow of the nematic catalyst solution, highly oriented films were obtained. The order parameter of the oriented sample, estimated from polarized absorption spectra, was about 0. 57. The maximum value of parallel electrical conductivity of the films doped with iodine was 4600 S/cm, while that of the films doped with arsenic pentafluoride was 11000 S/cm.
引用
收藏
页码：247 / 252
相关论文
共 50 条
  • [31] Synthesis and characterization of cholesteric liquid crystal elastomer films
    Feng, Ze-Long
    Fang, Lu-Xin
    Wan, Xin-Yi
    Gao, Yuan-Yuan
    Zhang, Xin-Yu
    Li, Fang-Yuan
    Tian, Mei
    MOLECULAR CRYSTALS AND LIQUID CRYSTALS, 2023, 753 (01) : 1 - 17
  • [32] ELECTRONIC-STRUCTURE OF THE POLYACETYLENE FILM ORIENTED BY A LIQUID-CRYSTAL SOLVENT UNDER MAGNETIC-FIELD
    PARK, YW
    LEE, YS
    KIM, YK
    LEE, CK
    PARK, C
    SHIRAKAWA, H
    AKAGI, K
    KITAGAKI, T
    KATAYAMA, S
    SYNTHETIC METALS, 1987, 17 (1-3) : 539 - 544
  • [33] SYNTHESIS, CHARACTERIZATION, AND PROPERTIES OF ALIGNED POLYACETYLENE FILMS
    SHIRAKAWA, H
    AKAGI, K
    KATAYAMA, S
    ARAYA, K
    MUKOH, A
    NARAHARA, T
    JOURNAL OF MACROMOLECULAR SCIENCE-CHEMISTRY, 1988, A25 (5-7): : 643 - 654
  • [34] MORPHOLOGY OF THIN LIQUID-CRYSTAL FILMS AND PHOTOPOLYMERIZED ALIGNMENT LAYERS
    KUMAR, S
    CULL, B
    SHI, Y
    SCHADT, M
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1995, 209 : 195 - COLL
  • [35] Ion implantation induced change in fibrillar morphology of polyacetylene films
    Koshida, N.
    Hirayama, N.
    Nuclear Instruments & Methods in Physics Research, Section B: Beam Interactions with Materials and Atoms, 1991, 59-60 (pt 2):
  • [36] Formation Mechanism of Helical Polyacetylene with Spiral Morphology in Asymmetric Reaction Field Consisting of Chiral Nematic Liquid Crystal
    Mori, Taizo
    Kyotani, Mutsumasa
    Akagi, Kazuo
    MACROMOLECULES, 2010, 43 (20) : 8363 - 8372
  • [37] GROWTH AND MORPHOLOGY OF UNDOPED AND DOPED POLYACETYLENE THIN-FILMS
    ROLLAND, M
    ABADIE, MJM
    CADENE, M
    REVUE DE PHYSIQUE APPLIQUEE, 1984, 19 (03): : 187 - 190
  • [38] THE MORPHOLOGY AND STRUCTURE OF POLYACETYLENE-POLYBUTADIENE GRAFT COPOLYMER FILMS
    PORZIO, W
    BOLOGNESI, A
    CATELLANI, M
    DESTRI, S
    MEILLE, SV
    PEDEMONTE, E
    MOLECULAR CRYSTALS AND LIQUID CRYSTALS, 1985, 117 (1-4): : 71 - 74
  • [39] Laser ablation of films and suspended particles in a solvent. Formation of cluster and colloid solutions
    Fojtik, A.
    Henglein, A.
    Berichte der Bunsengesellschaft fuer Physikalische Chemie, 1993, 97 (02):
  • [40] Optical properties of solvent-cast polarizer films for liquid crystal displays
    Greener, Jehuda
    Chen, Janglin
    IDMC 05: PROCEEDINGS OF THE INTERNATIONAL DISPLAY MANUFACTURING CONFERENCE 2005, 2005, : 177 - 180
12345