INFLUENCE OF NICKEL ON SCALING RESISTANCE OF 2 ″ONE QUARTER″ CR-1 MO BOILER TUBE ALLOYS.

被引：0
|
作者：
MANOLESCU, A.V.
ZEYA, M.
MAYER, P.
MUMMENHOFF, J.W.
机构：
来源：
| 1982年 / V 21卷 / N 9期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A SERIES OF STEELS CONTAINING 0 TO 5 WTP NI WERE OXIDIZED AT 550, 650, AND 800 C IN STEAM AND AIR. THE SCALING PROCESS FOLLOWS A PARABOLIC RATE LAW. THE OXIDE PHASES ON THE SCALESCONSISTED OF HEMATITE, MAGNETITE, AND WUSTITE. AT 550 C, THE RATE OF CORROSION INCREASED SLIGHTLY WITH NI. AT 650 AND 800 C, THE OXIDATION RATE DECREASED WITH INCREASING NI CONTENT.
引用
收藏
页码：9 / 13
相关论文
共 50 条
  • [21] ELECTRON BEAM WELDING OF 2 one quarter CR-1Mo STEEL FOR TURBINE CASING (REPORT 1).
    Kita, Hisanao
    Nakazaki, Takamitsu
    Akutsu, Yoji
    Kobayashi, Kei
    Urushidani, Haruo
    Kirihara, Seishin
    Yoshioka, Takatoshi
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 1986, 4 (01): : 35 - 40
  • [22] HOT CORROSION OF 2.25CR-1MO BOILER TUBE STEEL AND ITS WELDMENTS .2. CORROSION MECHANISM
    AHILA, S
    IYER, SR
    RADHAKRISHNAN, VM
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1994, 47 (2-3): : 183 - 191
  • [23] INFLUENCE OF PREHEATING AND POSTWELD HEATING ON HAZ PROPERTIES IN 1Cr-1Mo- one quarter V AND 13Cr-4Ni STEELS.
    Natarajan, B.
    Ravichandran, C.P.
    WRI Keywords (Welding Research Institute, Tiruchirapalli, India), 1983, 4 (02): : 57 - 63
  • [24] HEAVY SECTION 2 1/4 Cr-1 Mo STEEL PLATES WITH GOOD SOUNDNESS AND GOOD RESISTANCE AGAINST ENVIRONMENTAL EMBRITTLEMENT.
    Tagawa, Hisatoshi
    Tsuchida, Yutaka
    Yamada, Makoto
    Ikoma, Tsutomu
    Tanaka, Junichi
    Takeshige, Kenji
    Nippon Kokan technical report overseas, 1981, (33): : 17 - 30
  • [25] EFFECT OF VARIOUS HEAT-TREATMENTS ON THE OXIDATION BEHAVIOUR OF 2 one quarter Cr-1Mo STEEL.
    Khanna, A.S.
    Singh Raman, R.K.
    Gnanamoorthy, J.B.
    Key Engineering Materials, 1987, 20-28 (pt 1-4)
  • [26] EFFECT OF NITROGEN AND CARBON ON NOTCH TOUGHNESS OF 2 one quarter Cr-1Mo STEEL WELD METAL.
    Hojo, Itsuo
    Yamamoto, Shigeaki
    KOBELCO Technology Review, 1988, (03): : 31 - 34
  • [27] STUDY ON HIGH TEMPERATURE CREEP STRENGTH AND EMBRITTLEMENT DURING SERVICE OF ELECTRON BEAM WELDED JOINT - ELECTRON BEAM WELDING OF 2 one quarter Cr-1 Mo STEEL FOR STEAM TURBINE CASING.
    Kita, Hisanao
    Nakazaki, Takamitsu
    Akutsu, Yoji
    Kobayashi, Kei
    Urushidani, Haruo
    Kirihara, Seishin
    Yoshioka, Takatoshi
    1600, (04):
  • [28] Corrosion Resistance of Austenitic Cr-Ni-Mo Steels and Nickel-Base Ni-Cr-Mo Alloys in Fluosilicic Acid, H2SiF6.
    Kiesheyer, Heinrich
    Lennartz, Gustav
    DEW Technische Berichte, 1973, 13 (02): : 89 - 93
  • [29] REHEAT CRACKING IN 2 one quarter Cr1Mo SUBMERGED ARC WELD METAL - 2. RESULTS AND DISCUSSION.
    Hunter, A.N.R.
    Metal construction, 1982, 14 (05): : 266 - 270
  • [30] Influence of Alloy Grain Size on High Temperature Corrosion Behavior of 2.25 Cr-1 Mo Steel in SO2+O2 Atmosphere
    Ghosh, D.
    Mitra, S. K.
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2012, 31 (06) : 727 - 731
12345