PRIMARY CARBIDE IN CENTRIFUGALLY CAST SPHEROIDAL GRAPHITE IRON PIPE.

被引：0
|
作者：
Duerdin, E.C.
Schofield, R.
机构：
来源：
British Foundryman | 1976年 / 69卷 / pt 12期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The work described was undertaken as part of a broader investigation of centrifugally cast spheroidal graphite iron pipe. It describes some effects of variations in silicon, manganese, chromium, and phosphorus content of the iron on carbide formation and subsequent decomposition during heat treatment. The effect of carbide on tensile and impact properties and the fracture mechanisms involved were also determined.
引用
收藏
页码：316 / 322
相关论文
共 50 条
  • [1] FATIGUE-STRENGTH OF CENTRIFUGALLY CAST SPHEROIDAL GRAPHITE IRON PIPE
    TANAKA, K
    MATSUOKA, S
    ENGINEERING FRACTURE MECHANICS, 1979, 12 (02) : 221 - 230
  • [2] Weldability of spheroidal graphite cast iron
    Cembrero, Jesús
    Pascual, Manuel
    Revista de Metalurgia (Madrid), 35 (06): : 392 - 401
  • [3] Weldability of spheroidal graphite cast iron
    Cembrero, J
    Pascual, M
    REVISTA DE METALURGIA, 1999, 35 (06) : 392 - 401
  • [4] Austempering of spheroidal graphite cast iron
    El-Baradie, ZM
    Ibrahim, MM
    El-Sisy, IA
    Abd El-Hakeem, AA
    MATERIALS SCIENCE, 2004, 40 (04) : 523 - 528
  • [5] Austempering of spheroidal graphite cast iron
    Z. M. El-Baradie
    M. M. Ibrahim
    I. A. El-Sisy
    A. A. Abd El-Hakeem
    Materials Science, 2004, 40 : 523 - 528
  • [6] BRITISH GAS LOCATES JOINTS IN CAST IRON PIPE.
    Anon
    Pipe line industry Houston, Tex., 1986, 65 (03):
  • [7] SUPPORTS AND ANCHORS FOR HUBLESS CAST IRON SOIL PIPE.
    Konen, Thomas P.
    1600, (58):
  • [8] FORMATION OF SPHEROIDAL GRAPHITE IN CAST-IRON
    SELYANIN, IF
    KHRAPOV, AY
    PERMYAKO.AA
    STEEL IN THE USSR, 1972, 2 (10): : 842 - 843
  • [9] International standard for spheroidal graphite cast iron
    1600, Institute of Cast Metals Engineers (178):
  • [10] Formation of microstructures in the spheroidal graphite cast iron
    Wang, S.
    Daloz, D.
    Bruneseaux, F.
    Lesoult, G.
    3RD INTERNATIONAL CONFERENCE ON ADVANCES IN SOLIDIFICATION PROCESSES, 2012, 27
12345