Effect of long-term temperature and pressure hydrogen exposure on fracture and fatigue behaviors of Cr-Mo steel

被引：0
|
作者：
Li, Xiaogang
Li, Ming
Dong, Chaofang
Chen, Hua
机构：
来源：
Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2002年 / 24卷 / 04期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [31] CRACK INITIATION AND PROPAGATION UNDER HYDROGEN-ENHANCED FATIGUE OF A CR-MO STEEL FOR GASEOUS HYDROGEN STORAGE
    Briottet, Laurent
    Escot, Marielle
    Moro, Isabelle
    Tamponi, Gian Marco
    Furtado, Jader
    Solin, Jussi
    Bortot, Paolo
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2014, VOL 6B, 2014,
  • [32] Carbide transformations in Cr-Mo steels during long-term ageing and operation
    NPO 'TsKTI' im. I.I. Polzunova, Sankt-Peterburg, Russia
    Metalloved Term Obrab Met, 9 (9-13):
  • [33] Carbide transformations in Cr-Mo steels in the process of long-term aging and operation
    Pigrova, GD
    Sedov, VM
    Archakov, YI
    METAL SCIENCE AND HEAT TREATMENT, 1997, 39 (9-10) : 371 - 375
  • [34] FRACTURE TOUGHNESS AFTER LONG-TERM AGING IN 9CR-1MO-V STEEL FOR PRESSURE VESSELS
    Miyamura, Takeo
    Nanba, Shigenobu
    Nakanishi, Tomoaki
    Yamada, Masato
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2014, VOL 6B, 2014,
  • [35] Hydrogen-related degradation of fracture properties and altered fracture behavior of Cr-Mo steel used in hydrogen stationary vessels
    Nguyen, Thanh Tuan
    Park, Jaeyeong
    Bae, Kyung-Oh
    Baek, Un Bong
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2024, 53 : 1009 - 1024
  • [36] The behavior of electroplated hard-chromium on Cr-Mo steel subject to long-term annealing at 250°C
    Huang, CA
    Li, KC
    Lin, W
    Liao, MC
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 403 (1-2): : 222 - 226
  • [37] FATIGUE-LIFE AND LEAK-BEFORE-BREAK ASSESSMENTS OF CR-MO STEEL PRESSURE VESSELS WITH HIGH-PRESSURE GASEOUS HYDROGEN
    Yamabe, Junichiro
    Toga, Hisatake
    Awane, Tohru
    Matsunaga, Hisao
    Hamada, Shigeru
    Matsuoka, Saburo
    ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2014, VOL 6B, 2014,
  • [38] Combined Effect of Temper and Hydrogen Embrittlement on Threshold for Hydrogen-Induced Fracture in Cr-Mo Steels
    Shimazu, Hidenori
    Konosu, Shinji
    Tanaka, Yoichi
    Yuga, Masao
    Yamamoto, Hiroshi
    Ohtsuka, Naotake
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2013, 135 (02):
  • [39] Combined Effect of Temper and Hydrogen Embrittlement on Threshold for Hydrogen-Induced Fracture in Cr-Mo Steels
    Shimazu, Hidenori
    Konosu, Shinji
    Tanaka, Yoichi
    Yuga, Masao
    Yamamoto, Hiroshi
    Ohtsuka, Naotake
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, PVP 2012, VOL 6, PTS A AND B, 2012, : 825 - 833
  • [40] HIGH-TEMPERATURE, HIGH-CYCLE FATIGUE PROPERTIES OF Cr-Mo ALLOY STEEL PLATES FOR PRESSURE VESSELS.
    Kanazawa, Kenji
    Yamaguchi, Koji
    Sato, Morio
    Transactions of National Research Institute for Metals (Tokyo), 1981, 23 (02): : 88 - 94
12345