EFFECT OF OXYGEN ON THE WETTABILITY OF SOLID OXIDE BY MOLTEN IRON.

被引：21
|
作者：
Ogino, Kazumi
Nogi, Kiyoshi
Koshida, Yukio
机构：
来源：
| 1600年 / 59期
关键词：
531 Metallurgy and Metallography - 545 Iron and Steel;
D O I：
10.2355/tetsutohagane1955.59.10_1380
中图分类号：
学科分类号：
摘要：
By using the sessile drop method, the wettability of solid oxide (sintered alumina and sapphire) by molten iron was measured at 1600 degree C in atmospheres having different oxygen potentials. The solidified metal-oxide interface was observed with the optical microscope and EPMA. It was found that the surface tension and contact angle of molten iron on alumina decrease with increasing oxygen content in the metal, whereas the work of adhesion increases. Iron diffuses into the grain boundaries of sintered alumina.
引用
收藏
相关论文
共 50 条
  • [31] THE EFFECT OF OXYGEN-CONTENT IN MOLTEN IRON ON THE INTERFACIAL-TENSION BETWEEN MOLTEN IRON AND SLAG
    OGINO, K
    HARA, S
    MIWA, T
    KIMOTO, S
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 24 (07) : 522 - 531
  • [32] STUDY OF THE EQUILIBRIUM OF Ce-S-O IN MOLTEN IRON.
    Wang Changzhen
    Wang Fuzhen
    Du Yingmin
    Zhang Xiaoping
    Jinshu Xuebao/Acta Metallurgica Sinica, 1980, 16 (01): : 83 - 90
  • [33] INFLUENCE OF Bi AND Al ON CARBON DIFFUSION IN MOLTEN CAST IRON.
    Komarov, O.S.
    Tul'ev, V.D.
    1600,
  • [34] EQUILIBRIA BETWEEN RARE EARTH ELEMENTS AND SULFUR IN MOLTEN IRON.
    Han, Qiyong
    Dong, Yuanchi
    Feng, Xian
    Xiang, Changxiang
    Yang, Sifu
    Metallurgical transactions. B, Process metallurgy, 1985, 16 B (04): : 785 - 792
  • [35] Shape and Size of Gas Bubbles in Water, Mercury, and Molten Iron.
    Patel, Pervez
    1600, (44):
  • [36] EFFECTS OF SELENIUM AND TELLURIUM ON THE SURFACE-TENSION OF MOLTEN IRON AND THE WETTABILITY OF ALUMINA BY MOLTEN IRON
    OGINO, K
    NOGI, K
    YAMASE, O
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (03) : 234 - 239
  • [37] NUCLEATION MECHANISMS OF ALUMINA DEOXIDATION PRODUCTS IN THE QUIESCENT MOLTEN IRON.
    Kusakawa, Takaji
    Shiohara, Yuh
    Araki, Satoshi
    1978, (29): : 7 - 13
  • [38] REDUCTION OF MOLTEN IRON OXIDE-BASED SLAGS BY SOLID GRAPHITE
    HARA, S
    OGINO, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1990, 76 (03): : 360 - 367
  • [39] NEW SPHEROIDIZATION PROCESS FOR HIGH-SULPHUR MOLTEN IRON.
    Zhu, Yuanka
    Peng, Yujiang
    Hong, Yanruo
    Su, Luiji
    Yu, Xuebin
    Jinshu Xuebao/Acta Metallurgica Sinica, 1984, 20 (04): : 177 - 184
  • [40] INFLUENCE OF SULFUR ON DISSOLVING BEHAVIOURS OF GRAPHITE IN MOLTEN CAST IRON.
    Kayama, Nobutaro
    Suzuki, Katsumi
    Report of the Castings Research Laboratory, Waseda University, 1979, (30): : 61 - 67
12345