COMPARISON OF FATIGUE PROCESSES IN 0. 45%C STEEL SPECIMENS POLISHED UNDER DIFFERENT CONDITIONS.

被引：0

作者：

Nisitani, Hironobu ^{[1
]}

Imai, Ryoichi ^{[1
]}

机构：

[1] Kyushu Univ, Faculty of Engineering,, Fukuoka, Jpn, Kyushu Univ, Faculty of Engineering, Fukuoka, Jpn

来源：

Bulletin of the JSME | 1985年 / 28卷 / 245期

关键词：

FATIGUE PROCESS - MICROCRACKS - ROTATING BENDING FATIGUE - SURFACE STATES CHANGE;

D O I：

10.1299/jsme1958.28.2503

中图分类号：

学科分类号：

摘要：

引用

页码：2503 / 2510

共 50 条

[31] Investigation of Fatigue Resistance of Specimens of Different Steels Under the Conditions of Combined Effects of Cyclic Bending and Torsion.
Belkin, L.M.
Filimonov, G.N.
Belkin, M.Ya.
Vishnevskii, A.P.
Volkov, I.B.
Problemy Prochnosti, 1986, (01): : 22 - 24
[32] FRETTING FATIGUE IN JIS S45C STEEL UNDER 2-STEP BLOCK LOADING
MUTOH, Y
TANAKA, K
KONDOH, M
JSME INTERNATIONAL JOURNAL, 1987, 30 (261) : 386 - 393
[33] On the correlation of temperature harmonic content with energy dissipation in C45 steel samples under fatigue loading
Cappello, Riccardo
Meneghetti, Giovanni
Ricotta, Mauro
Pitarresi, Giuseppe
MECHANICS OF MATERIALS, 2022, 168
[34] Comparison of responses of different types of steel alloys under the same loading and environmental conditions
Brnic, Josip
Krscanski, Sanjin
Brcic, Marino
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART L-JOURNAL OF MATERIALS-DESIGN AND APPLICATIONS, 2021, 235 (06) : 1194 - 1202
[35] Ratcheting fatigue behaviour of 42CrMo4 steel under different heat treatment conditions
Kreethi, R.
Mondal, A. K.
Dutta, Krishna
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 679 : 66 - 74
[36] Comparison of fatigue characteristics and failure analysis of Ni-based superalloy subjected to thermomechanical fatigue under different phase conditions
Dao, Van Hung
Yun, Hee Soo
Jeon, Sang Koo
Park, Jaeyeong
Nahm, Seung Hoon
ENGINEERING FAILURE ANALYSIS, 2024, 165
[37] A comparison of short fatigue crack growth (SFCG) rates, in a medium strength steel, under in-air and corrosion fatigue loading conditions
Hu, H
Akid, R
HYDROGEN EFFECTS ON MATERIAL BEHAVIOR AND CORROSION DEFORMATION INTERACTIONS, 2003, : 617 - 628
[38] Fatigue crack growth behaviour of SM45C steel under mixed-mode I and II loading
You, BR
Lee, SB
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1998, 21 (09) : 1037 - 1048
[39] Persistency of corrosion inhibitor films on C-steel under multiphase flow conditions. Part I: The jet-cylinder arrangement
Heeg, B
Moros, T
Klenerman, D
CORROSION SCIENCE, 1998, 40 (08) : 1303 - 1311
[40] Persistency of corrosion inhibitor films on C-steel under multiphase flow conditions. Part II: optical SHG and electrochemical studies
Department of Chemistry, University of Cambridge, Lensfield Road, Cambridge, CB2 1EW, United Kingdom
Corros. Sci., 8 (1313-1329):

← 1 2 3 4 5 →