DIRECTLY COOLED DRAWING OF HIGH-CARBON STEEL WIRE.

被引：0
|
作者：
Petkovic, Dominique
机构：
来源：
Wireworld international | 1985年 / 27卷 / 10期
关键词：
TEMPERATURE CONTROL - Cooling - WIRE - Manufacture;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Attempts to lower fabrication costs in the wire manufacturing industry are aimed principally at increasing the drawing speed and so raising the rate of production. However, as the drawing speed rises so too does the wire temperature. When drawing high-carbon steel, the mechanical properties deteriorate very rapidly once the temperature climbs above 180 degree C. Trials on a new direct cooling system have shown that an increase in drawing speed of over 30% is possible without the critical temperature limit being overstepped.
引用
收藏
页码：226 / 227
相关论文
共 50 条
  • [41] DENSITY VARIATION OF A HIGH-CARBON STEEL WIRE WITH WIREDRAWING STRAIN
    WRIEDT, HA
    HUGHES, HA
    METALLURGICAL TRANSACTIONS, 1970, 1 (12): : 3457 - &
  • [42] High-carbon wire rod made of high-chromium steel
    Sychkov, A. B.
    Zhigarev, M. A.
    Perchatkin, A. V.
    Berkovskii, V. A.
    Krulik, A. I.
    METALLURGIST, 2006, 50 (3-4) : 183 - 188
  • [43] RAPID HEATING PATENTING OF HIGH-CARBON STEEL WIRE RODS
    TAKAHASHI, E
    KATO, T
    ARAKAWA, J
    KOUOKA, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1977, 17 (06) : 359 - 364
  • [44] ROLLING OF HIGH-CARBON WIRE RODS IN BHILAI STEEL PLANT
    BISHNOI, YPS
    TUDEKAR, SG
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1970, 208 (DEC): : 1083 - &
  • [45] High-carbon wire rod made of steel microalloyed with vanadium
    Parusov, VV
    Sychkov, AB
    Derevyanchenko, IV
    Perchatkin, AV
    Parusov, ÉV
    Zhigarev, MA
    METALLURGIST, 2004, 48 (11-12) : 618 - 625
  • [46] High-carbon wire rod made of steel microalloyed with vanadium
    V. V. Parusov
    A. B. Sychkov
    I. V. Derevyanchenko
    A. V. Perchatkin
    É. V. Parusov
    M. A. Zhigarev
    Metallurgist, 2004, 48 : 618 - 625
  • [47] MICROSTRUCTURE AND DEFORMATION OF HIGH CARBON WIRE.
    Lambert, N.
    Greday, T.
    Metallurgical Reports CRM (Centre de Recherches Metallurgiques), 1974, (40): : 43 - 73
  • [48] Evolution of void volume fraction for simulating inner fracture defects related to in drawing of high-carbon steel wire rods
    Komori, K.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2008, 50 (02) : 157 - 166
  • [49] Considerations Regarding the Annealing of Low Carbon Steel Wire.
    Avramescu, S.
    Metalurgia Bucuresti, 1982, 34 (08): : 421 - 423
  • [50] PRECIPITATION ZONE OF PROEUTECTOID CEMENTITE IN HIGH-CARBON STEEL WIRE RODS
    TOGASHI, F
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1393 - 1393
12345