OBSERVATION OF FRACTURE SURFACES OF TRC TEST SPECIMENS WITH SCANNING ELECTRON MICROSCOPE.

被引：0

作者：

Masumoto, Isao

Terai, Kiyoshi

Yamada, Sotaro

Kutsuna, Muneharu

机构：

来源：

| 1600年 / 05期

关键词：

STEEL TESTING - Fracture;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Tensile restraint cracking tests of HT-100, a steel with hydrogen embrittlement, showed intergranular fracture and quasicleavage fracture. Specimens with medium hydrogen embrittlement showed, in their root sections, quasicleavage fracture surface. The width of such area increased as the applied stress decreased and the fracture time was prolonged. Specimens with little hydrogen embrittlement showed dimple patterns in their root sections and ductile fracture surfaces.

引用

共 50 条

[21] STUDYING BONE REGENERATION WITH THE SCANNING ELECTRON MICROSCOPE.
Draenert, K.
Scanning Electron Microscopy, 1983, v (pt 1) : 247 - 254
[22] AUTOMATED FIBER COUNTING IN THE SCANNING ELECTRON MICROSCOPE.
Stott, W.R.
Meranger, J.C.
Scanning Electron Microscopy, 1984, v : 583 - 588
[23] Investigation of the Porosity of Sandstones by Scanning Electron Microscope.
Gaida, Karl Heinz
Ruehl, Walter
Zimmerle, Winfried
Erdoel-Erdgas-Zeitschrift, 1973, 89 (09): : 336 - 343
[24] Fault Analysis of Semiconductors with the Scanning Electron Microscope.
Schaefer, Wolfgang
Niederauer, Klaus
1600, (34):
[25] Schizosaccharomyces japonicus through scanning electron microscope.
Benevelli, M
Zambonelli, C
Papa, F
Grazia, L
ANNALI DI MICROBIOLOGIA ED ENZIMOLOGIA, 1996, 46 : 29 - 38
[26] Charging identification and compensation in the scanning electron microscope.
Wong, WK
Thong, JTL
Phang, JCH
PROCEEDINGS OF THE 1997 6TH INTERNATIONAL SYMPOSIUM ON THE PHYSICAL & FAILURE ANALYSIS OF INTEGRATED CIRCUITS, 1997, : 97 - 102
[27] High Resolution Scanning Transmission Electron Microscope.
Mueller, Karl Heinz
Krisch, Burkhard
1600, : 76 - 57
[28] MEASUREMENT OF SHORT LENGTHS WITH A SCANNING ELECTRON MICROSCOPE.
Bogdankevich, O.V.
Zhelkobaev, Zh.
Kalendin, V.V.
Kudeyarov, Yu.A.
Nevsorova, L.N.
Measurement Techniques, 1985, 28 (11) : 957 - 961
[29] INVESTIGATION OF MAGNETIC STRUCTURES WITH THE SCANNING ELECTRON MICROSCOPE.
Balk, L.J.
Elsbrock, J.B.
1600, (0v):
[30] TENSILE TEST OF FOIL SPECIMENS OF IRON SINGLE CRYSTALS AT ROOM AND LOW TEMPERATURES UNDER OBSERVATION IN HIGH VOLTAGE ELECTRON MICROSCOPE.
Saka, H.
Noda, K.
Imura, T.
1600, (04):

← 1 2 3 4 5 →