Characteristics of heat-affected zone cracking in cast alloy 718 - a study on weldability of cast alloy 718 (Report 1)

被引：0
|
作者：
Woo, Insu
Nishimoto, Kazutoshi
Tanaka, Katsuyuki
Shirai, Makoto
机构：
来源：
Welding Research Abroad | 1999年 / 45卷 / 11期
关键词：
Crack propagation - Grain boundaries - Metal castings - Nickel alloys - Niobium compounds;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Characteristics of the heat-affected zone cracking of cast alloy 718 has been investigated using the bead on plate test and microscopic observation for isothermally processed specimens. The results obtained in this study are summarized as follows: (1) It was clarified that cracking in HAZ of cast alloy 718 was intergranular cracking which was caused by liquation of grain boundary phases. (2) According to the microscopic observation of specimens heated at various temperatures, incipient melting of the grain boundaries was found to occur at the temperature of 1383 K and above. (3) The Laves cluster was observed to liquate at the ternary eutectic temperature of 1383 K, which was lower than the NbC liquation temperature of 1413 K. (4) The liquation cracking in HAZ of cast alloy 718 was considered to be caused by constitutional liquation of Laves cluster at the grain boundaries.
引用
下载
收藏
相关论文
共 50 条
  • [41] Use of Friction Stir Processing for Improving Heat-Affected Zone Liquation Cracking Resistance of a Cast Magnesium Alloy AZ91D
    Karthik, G. M.
    Ram, G. D. Janaki
    Kottada, Ravi Sankar
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2017, 48 (06): : 3270 - 3280
  • [42] The effect of rejuvenation heat treatments on the repair weldability of wrought Alloy 718
    Qian, M
    Lippold, JC
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 340 (1-2): : 225 - 231
  • [43] The effect of cooling rate of solidification on microstructure and alloy element segregation of as cast alloy 718
    Jingchen, Z
    Ping, Y
    SUPERALLOYS 718, 625, 706 AND VARIOUS DERIVATIVES, 2001, : 133 - 140
  • [44] Weldability of superalloys alloy 718 and ATI® 718Plus™ - A study performed by Varestraint testing
    Jacobsson, Jonny
    Andersson, Joel
    Brederholm, Anssi
    Hanninen, Hannu
    MATERIALS TESTING, 2017, 59 (09) : 769 - 773
  • [45] THE RELATIONSHIP BETWEEN CARBON CONTENT, MICROSTRUCTURE, AND INTERGRANULAR LIQUATION CRACKING IN CAST NICKEL ALLOY-718
    THOMPSON, RG
    MAYO, DE
    RADHAKRISHNAN, B
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02): : 557 - 567
  • [46] MECHANICAL-PROPERTIES AND MICROSTRUCTURE OF CENTRIFUGALLY CAST ALLOY-718
    MICHEL, DJ
    SMITH, HH
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (07): : 1295 - 1306
  • [47] WELDABILITY FORMULA OF HIGH STRENGTH STEELS RELATED TO HEAT-AFFECTED ZONE CRACKING
    ITO, Y
    BESSYO, K
    SUMITOMO SEARCH, 1969, (01): : 59 - &
  • [48] Metallurgical factors contributing to HAZ cracking susceptibility in cast alloy 718 welds and its improvement by cerium addition
    Insu Woo
    Kazutoshi Nishimoto
    Metals and Materials International, 2001, 7 : 241 - 249
  • [49] Influence of electron beam welding parameters and metallurgical factors on intergranular liquation cracking susceptibility of cast alloy 718
    Woo, I
    Kang, CY
    Nishimoto, K
    METALS AND MATERIALS INTERNATIONAL, 2001, 7 (04): : 349 - 357
  • [50] Metallurgical factors contributing to HAZ cracking susceptibility in cast alloy 718 welds and its improvement by cerium addition
    Woo, I
    Nishimoto, K
    METALS AND MATERIALS-KOREA, 2001, 7 (03): : 241 - 249
12345