Properties of long afterglow SrAl2O4:Eu2+, Dy3+ phosphor

被引：0
|
作者：
Geng, Jie [1 ]
Wu, Zhao-Ping [1 ]
Chen, Wei [1 ]
Luo, Lan [1 ]
机构：
[1] Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
来源：
Wuji Cailiao Xuebao/Journal of Inorganic Materials | 2003年 / 18卷 / 02期
关键词：
Solid state reactions - Emission spectroscopy - Thermoluminescence;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
SrAl2O4:Eu2+, Dy3+ powder phosphors were synthesized by solid-state reaction process. Based on the XRD peaks, the powder phosphors were identified as SrAl2O4phase, which is monoclinic(a=8.4428Å, b=8.822Å, c=5.1607Å, β=93.415°). These phosphors exhibited broadband peaks in both the excitation and emission spectra. The excitation peaks lied between 300nm and 450nm, and the main emission peaks lied around 518nm. The results indicate that the luminescence of these phosphors are due to 4f65d → 4f7(8S7/2) transition of Eu2+. And its luminescence decay consists of the initial fast process and the later extremely slow process. The trap level of phosphors was analyzed through thermoluminescent spectra, which consists two peaks. This means that there are two electron traps in SrAl2O4:Eu2+, Dy3+, which can cause the long afterglow of the phosphors. The trap depths measured are 0.38eV and 1.34eV respectively.
引用
收藏
页码：480 / 484
相关论文
共 50 条
  • [21] Synthesis and properties of SrAl2O4:Eu2+, Dy3+ nanowires
    Li, Zhi-jie
    Zhang, Yu-feng
    Wu, Xiao
    Qin, Chu-yang
    Shi, Gui-mei
    PHYSICS LETTERS A, 2017, 381 (40) : 3519 - 3522
  • [22] Synthesis of long afterglow SrAl2O4:: EU2+, Dy3+ phosphors through microwave route
    Geng, J
    Wu, Z
    JOURNAL OF MATERIALS SYNTHESIS AND PROCESSING, 2002, 10 (05) : 245 - 248
  • [23] Coordination encapsulation on SrAl2O4:Eu2+, Dy3+ phosphor and its characterization
    School of Chemical and Energy Engineering, South China University of Technology, Guangzhou 510640, China
    不详
    Wuji Cailiao Xuebao, 2007, 4 (642-646):
  • [24] Coordination encapsulation on SrAl2O4:Eu2+ Dy3+ phosphor and its characterization
    Yu, Sheng-Fei
    Pi, Pi-Hui
    Wen, Xiu-Fang
    Cheng, Jiang
    Yang, Zhuo-Ru
    JOURNAL OF INORGANIC MATERIALS, 2007, 22 (04) : 642 - 646
  • [25] Synthesis of Long Afterglow Phosphors Doped B SrAl2O4 : Eu2+, Dy3+ and Its Luminescent Properties
    Qiu Guanming
    Chen Yongjie
    Cui Jingqiang
    Geng Xiujuan
    Wang Hui
    Song Bo
    JOURNAL OF RARE EARTHS, 2007, 25 : 86 - 89
  • [26] Effects of PEG on Properties of SrAl2O4:Eu2+, Dy3+ Long Afterglow Phosphors Prepared by Combustion Synthesis
    Liu, Xiaoxia
    Liang, Min
    Peng, Guihua
    Liang, Zhenhua
    HIGH-PERFORMANCE CERAMICS VII, PTS 1 AND 2, 2012, 512-515 : 1494 - +
  • [27] Charging curves and excitation spectrum of long persistent phosphor SrAl2O4:Eu2+, Dy3+
    Jia, DD
    OPTICAL MATERIALS, 2003, 22 (01) : 65 - 69
  • [28] Preparing and testing the reliability of long-afterglow SrAl2O4:Eu2+, Dy3+ phosphor flexible films for temperature sensing
    Wang, Li
    Shang, Zhaojiang
    Shi, Mingming
    Cao, Peiyuan
    Yang, Bobo
    Zou, Jun
    RSC ADVANCES, 2020, 10 (19) : 11418 - 11425
  • [29] Effect of nominal substitution of Dy3+ for host cations in SrAl2O4: Eu2+ phosphor on phase evolution and long afterglow luminescence
    Shin, Hyunho
    Ullah, Shafgat
    Chung, Kwanghyun
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 544 : 181 - 187
  • [30] Synthesis of green phosphor SrAl2O4: Eu2+, Dy3+: Rietveld refinement and optical properties
    Roslan, N. N. N.
    Razali, W. A. W.
    Tamuri, A. R.
    Azhan, H.
    Mohamed, Z.
    CHALCOGENIDE LETTERS, 2022, 19 (02): : 83 - 91
12345