Properties of long afterglow SrAl2O4:Eu2+, Dy3+ phosphor

被引：0
|
作者：
Geng, Jie [1 ]
Wu, Zhao-Ping [1 ]
Chen, Wei [1 ]
Luo, Lan [1 ]
机构：
[1] Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
来源：
Wuji Cailiao Xuebao/Journal of Inorganic Materials | 2003年 / 18卷 / 02期
关键词：
Solid state reactions - Emission spectroscopy - Thermoluminescence;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
SrAl2O4:Eu2+, Dy3+ powder phosphors were synthesized by solid-state reaction process. Based on the XRD peaks, the powder phosphors were identified as SrAl2O4phase, which is monoclinic(a=8.4428Å, b=8.822Å, c=5.1607Å, β=93.415°). These phosphors exhibited broadband peaks in both the excitation and emission spectra. The excitation peaks lied between 300nm and 450nm, and the main emission peaks lied around 518nm. The results indicate that the luminescence of these phosphors are due to 4f65d → 4f7(8S7/2) transition of Eu2+. And its luminescence decay consists of the initial fast process and the later extremely slow process. The trap level of phosphors was analyzed through thermoluminescent spectra, which consists two peaks. This means that there are two electron traps in SrAl2O4:Eu2+, Dy3+, which can cause the long afterglow of the phosphors. The trap depths measured are 0.38eV and 1.34eV respectively.
引用
收藏
页码：480 / 484
相关论文
共 50 条
  • [1] Properties of long afterglow SrAl2O4:Eu2+, Dy3+ phosphor
    Geng, J
    Wu, ZP
    Chen, W
    Luo, L
    [J]. JOURNAL OF INORGANIC MATERIALS, 2003, 18 (02) : 480 - 484
  • [2] SrAl2O4:Eu2+, Nd3+ and Dy3+ long afterglow phosphor
    He, DW
    Lü, JH
    Cui, XL
    [J]. JOURNAL OF RARE EARTHS, 2003, 21 (02) : 146 - 148
  • [3] SrAl2O4∶Eu2+,Nd3+ and Dy3+ Long Afterglow Phosphor
    何大伟
    吕菁华
    崔兴龙
    [J]. Journal of Rare Earths, 2003, (02) : 146 - 148
  • [4] Synthesis of long afterglow SrAl2O4:Eu2+,Dy3+ phosphor by microemulsion method
    Chen, YJ
    Qiu, GM
    Geng, XJ
    Xiao, LJ
    Tian, YG
    Sun, YB
    [J]. JOURNAL OF RARE EARTHS, 2004, 22 : 34 - 37
  • [5] Long afterglow characteristics of γ-ray irradiated SrAl2O4:Eu2+,Dy3+ phosphor
    Yang F.
    Fu R.
    Tang Y.
    Gu X.
    Liu C.
    Cai J.
    [J]. Fu, Renli (renlifu@nuaa.edu.cn), 1600, Chinese Optical Society (37):
  • [6] Effect of Addition of Boron on the Long Afterglow Property of SrAl2O4: Eu2+, Dy3+ Phosphor
    Takeuchi, Nobuyuki
    Kishine, Kimiko
    [J]. MATERIALS TRANSACTIONS, 2021, 62 (07) : 1039 - 1045
  • [7] SrAl2O4: Eu2+,Dy3+:: Synthesis by flux method and long afterglow properties
    Wang, YH
    Song, XY
    Zhang, SH
    [J]. CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2006, 22 (01) : 41 - 46
  • [8] Thermal Stability of SrAl2O4: Eu2+, Dy3+ with Long Afterglow Phosphorescence
    Kim, Jin-Ho
    Lee, Seung-Yong
    Kim, Tae-Ho
    Han, Kyu-Sung
    Hwang, Kwang-Taek
    Cho, Woo-Seok
    [J]. JOURNAL OF THE KOREAN CERAMIC SOCIETY, 2014, 51 (06) : 618 - 622
  • [9] SrAl2O4:Eu2+,Dy3+ Long Afterglow Phosphor and Its Flexible Film for Optomechanical Sensing Application
    Achari, Akshay M.
    Perumalsamy, Vanishree
    Swati, Godavarthi
    Khare, Ayush
    [J]. ACS OMEGA, 2023, 8 (48): : 45483 - 45494
  • [10] The luminescent character of long-afterglow material SrAl2O4: EU2+, Dy3+
    Yang, ZP
    Liu, Z
    Zhu, SC
    [J]. MATERIALS, DEVICES, AND SYSTEMS FOR DISPLAY AND LIGHTING, 2002, 4918 : 413 - 417
12345