Optimized temperature conditions in continuous casting of Ti- containing stainless steel

被引：0
|
作者：
Garafutdinov, R.A. [1 ]
Baldaev, B.Ya. [1 ]
Savinova, N.G. [1 ]
Tsvetkov, M.A. [1 ]
机构：
[1] Cherepovetskij Metallurgicheskij, Kombinat, Cherepovets, Russia
来源：
Stal' | 1992年 / 03期
关键词：
Castings - Quality Control - Liquid Metals - Denitrification - Steel - Corrosion Resistance - Temperature Control - Optimization;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Increased quality of the surface of 08-12 Kh18N10T steel castings is promoted by maximum nitridation of metal during treatment outside the furnace and its suppression in continuous casting. Such effect is attained by decrease of the end temperature of out-furnace working down to 1565 ° C and not more then 45° C difference of metal temperatures in casting and intermediate ladles. Such innovation in casting of stainless Ti-containing steel according to the scheme ″100-t arc furnace conticaster″ provided to decrease slab spoilage due to surface defects by 2-3 times, and metal losses during stripping before slabbing from 6-7 to 4-5%.
引用
收藏
页码：27 / 28
相关论文
共 50 条
  • [41] Metallurgical investigation on fatigue failure of stainless steel chain in a continuous casting machine
    Pantazopoulos, G.
    Vazdirvanidis, A.
    ENGINEERING FAILURE ANALYSIS, 2009, 16 (05) : 1623 - 1630
  • [42] Application of New Continuous Casting Technologies in TISCO New Stainless Steel Project
    Li Zhi-bin
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2008, 15 : 59 - 66
  • [43] SOLIDIFICATION STRUCTURE OF STAINLESS-STEEL BILLET IN HORIZONTAL CONTINUOUS-CASTING
    UMEDA, Y
    SUGITANI, Y
    NAKAI, K
    ISHIHARA, K
    SAKANE, T
    FUKUSHIMA, Y
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1982, 22 (12) : B379 - B379
  • [44] Investigating the binding potential of continuous casting stainless steel slag by alkali activation
    Salman, Muhammad
    Cizer, Ozlem
    Pontikes, Yiannis
    Snellings, Ruben
    Vandewalle, Lucie
    Blanpain, Bart
    van Balen, Koen
    ADVANCES IN CEMENT RESEARCH, 2014, 26 (05) : 256 - 270
  • [45] Microstructure and solidification thermal parameters in thin strip continuous casting of a stainless steel
    Spinelli, JE
    Tosetti, JP
    Santos, CA
    Spim, JA
    Garcia, A
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 150 (03) : 255 - 262
  • [46] Experimental and analytical analysis of the high-temperature mechanical properties of steel under continuous casting conditions
    Pierer, R
    Bernhard, C
    Chimani, C
    Computational Methods and Experimental Measurements XII, 2005, 41 : 757 - 768
  • [47] Numerical simulations of solidification and hot tearing for continuous casting of duplex stainless steel
    Liu, Shan-shan
    Bai, Liang
    Wang, Bo
    Yaoi, Yu
    Huang, Jun-kai
    Chen, Zheng
    Zhang, Jie-yu
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2020, 27 (06) : 643 - 655
  • [48] Evolution of Different Inclusions during Ladle Treatment and Continuous Casting of Stainless Steel
    Bi, Yanyan
    Karasev, Andrey Vladimirovich
    Jonsson, Par Gran
    ISIJ INTERNATIONAL, 2013, 53 (12) : 2099 - 2109
  • [49] Compositional Evolution of Oxide Inclusions in Austenitic Stainless Steel during Continuous Casting
    Choi, Ja-Yong
    Kim, Sun-Koo
    Kang, Youn-Bae
    Lee, Hae-Geon
    STEEL RESEARCH INTERNATIONAL, 2015, 86 (03) : 284 - 292
  • [50] Numerical simulations of solidification and hot tearing for continuous casting of duplex stainless steel
    Shan-shan Liu
    Liang Bai
    Bo Wang
    Yu Yao
    Jun-kai Huang
    Zheng Chen
    Jie-yu Zhang
    Journal of Iron and Steel Research International, 2020, 27 : 643 - 655
12345