Characterization of superconducting (Tl,Bi)Sr2CaCu2Oy

被引：0
|
作者：
Superconductivity Technology Cent, Los Alamos, United States [1 ]
机构：
来源：
Phys C Supercond | / 3-4卷 / 358-364期
关键词：
Bismuth compounds - Calcium compounds - Composition effects - Magnetic hysteresis - Magnetic permeability - Oxide superconductors - Phase transitions - Strontium compounds - Superconducting transition temperature - Thallium compounds - X ray powder diffraction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The superconducting phase with mixed Tl and Bi, namely (Tl0.55Bi0.45)Sr2CaCu2Oy, was synthesized and characterized. Synthesis conditions were studied, and this phase, (Tl,Bi)-1212, was found to form preferentially to (Tl,Bi)-1223 when Sr was present with no Ba present. X-ray powder diffraction with Rietveld refinement provided structural data. The phase is tetragonal with a = 3.7988(4) A and c = 12.076(1) A, with space group symmetry P4/mmm, and with a platelet crystal morphology. Magnetic-susceptibility data gave an onset of superconductivity Tc at 94.9 ± 1.3 K with a Tcmid of 86.0 ± 1.1 K. Magnetic-hysteresis measurements showed that substantial flux pinning occurs in this phase at high temperatures.
引用
收藏
相关论文
共 50 条
  • [31] Nature of the vortex liquid in Bi2Sr2CaCu2Oy
    Tsuboi, T
    Hanaguri, T
    Maeda, A
    PHYSICAL REVIEW B, 1997, 55 (14) : R8709 - R8712
  • [32] Characteristic fields of a Bi2Sr2CaCu2Oy crystal
    Zavaritskii, VN
    JETP LETTERS, 2000, 71 (02) : 80 - 84
  • [33] Influence of Pb on structural and superconducting properties of rare earth modified Bi2Sr2CaCu2Oy
    Biju, A.
    Guruswamy, P.
    Syamaprasad, U.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2007, 466 (1-2): : 23 - 28
  • [34] Rapid synthesis of superconducting Bi2Sr2CaCu2Oy powders by sol-gel method
    Qi, Yang
    Chen, Wan-Shi
    Zhang, Cai-Bei
    Yang, Hua-Zhe
    Dongbei Daxue Xuebao/Journal of Northeastern University, 2006, 27 (04): : 465 - 468
  • [35] RECOVERY OF SUPERCONDUCTING PROPERTIES OF BI2SR2CACU2OY CRYSTALS IRRADIATED BY N+ IONS
    WANG, LB
    WU, WB
    ZHU, JS
    SUN, XF
    LI, XG
    ZHOU, G
    ZHANG, YH
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1995, 150 (02): : K19 - K22
  • [36] POTASSIUM SUBSTITUTION IN THE BI2SR2CACU2OY SUPERCONDUCTOR
    KRISHNA, BG
    CHANDRA, GR
    SURYANARAYANA, SV
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1994, 25 (2-3): : 153 - 158
  • [37] Potassium substitution in the Bi2Sr2CaCu2Oy superconductor
    Krishna, B.Gopala
    Chandra, G.Ravi
    Suryanarayana, S.V.
    Materials science & engineering. B, Solid-state materials for advanced technology, 1994, B25 (2-3): : 153 - 158
  • [38] EFFECT OF BA SUBSTITUTION FOR SR IN BI2SR2CACU2OY SUPERCONDUCTING FILMS PREPARED BY RF-SPUTTERING METHOD
    KANEMATSU, S
    ENOMOTO, H
    SHIN, JS
    OZAKI, H
    PHASE TRANSITIONS, 1993, 41 (1-4) : 179 - 184
  • [39] Growth of Bi2Sr2CaCu2Oy single crystals by a vertical Bridgman method and their characterization
    Tanaka, A
    Kishida, S
    Shibasaki, A
    Hosokawa, E
    Tokutaka, H
    JOURNAL OF CRYSTAL GROWTH, 1997, 182 (1-2) : 60 - 64
  • [40] CRITICAL CURRENT AS A FUNCTION OF TEMPERATURE IN SUPERCONDUCTING SINGLE-CRYSTAL (BI,PB)2SR2CACU2OY
    OYA, G
    AOYAMA, N
    KISHIDA, S
    TOKUTAKA, H
    PHYSICA C, 1991, 185 : 2453 - 2454
12345