ON CORROSION FATIGUE MECHANISMS FOR S45C AND SCM435 STEELS IN ROTATING BENDING.

被引：0

作者：

Masuda, Chitoshi

Nishijima, Satoshi

Abe, Takayuki

Sumiyoshi, Hideshi

机构：

来源：

Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A | 1984年 / 50卷 / 453期

关键词：

STEEL TESTING - Fatigue;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Morphology of surface damage and small cracks by the corrosion fatigue was studied for quenched and tempered carbon steel S45C and Cr-Mo steel SCM435 in a deionized water and 3% NaCl water environments under rotating bending at frequencies from 0. 03 to 30 Hz. In saline water the fatigue strength of the two steels decreased monotonously with increasing number of cycles and testing time, while in the pure water a kind of temporal fatigue limit was observed for frequencies higher than 3 Hz. In the latter case fatigue crack was arrested by the closure effect of corrosion porduct for certain periods but this was diminished by dissolution after enough long test duration.

引用

页码：1019 / 1025

共 40 条

[31] Effect of Cut-off Levels on Homology Fatigue Fracture Surface Analysis of Low Carbon Steel (JIS, S45C)
Kida, Katsuyuki
Ishida, Masayuki
Mizobe, Koshiro
Nakane, Kazuaki
FRONTIERS OF MANUFACTURING SCIENCE AND MEASURING TECHNOLOGY V, 2015, : 790 - 797
[32] Changes in magnetic field intensities around fatigue crack tips of medium carbon low alloy steel (S45C, JIS)
Kida, K.
Santos, E. C.
Uryu, M.
Honda, T.
Rozwadowska, J. A.
Saruwatari, K.
INTERNATIONAL JOURNAL OF FATIGUE, 2013, 56 : 33 - 41
[33] Construction of a Corrosion Test Chamber for the Installation in a Rotating Bending Machine for Corrosion Fatigue Tests of Cr-Mn-N Austenitic Steels Used in the Oil-field Industry
Leidinger, Dominik
Holper, Bernd
Sommitsch, Christof
BHM Berg- und Huttenmannische Monatshefte, 2015, 160 (09): : 419 - 425
[34] New evaluation method of crack initiation limit in notched specimen: effect of notch shape on aspect ratio of low carbon alloy steels (JIS, S15C, S35C and S45C)
Matsueda, T.
MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 48 - 51
[35] Effect of material flow behavior on the formation of interfacial reaction layers and fatigue performance of dissimilar friction stir welded S45C and AA6061-T6
Gao, Kun
Liu, Guiqi
Wang, Guangdong
Basak, Soumyabrata
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2024, 133 (9-10): : 4833 - 4844
[36] Effect of material flow behavior on the formation of interfacial reaction layers and fatigue performance of dissimilar friction stir welded S45C and AA6061-T6
Gao, Kun
Liu, Guiqi
Wang, Guangdong
Basak, Soumyabrata
International Journal of Advanced Manufacturing Technology, 1600, 133 (9-10): : 4833 - 4844
[37] VALIDITY OF PARIS'S RULE FOR A HEAT-TREATED 0. 54% C STEEL SPECIMEN UNDER ROTATING BENDING FATIGUE.
Nisitani, Hironobu
Goto, Masahiro
Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (474): : 384 - 389
[38] Effect of a Thermochemical Surface Treatment (Nitriding) on the Fatigue Strength and the Alternation Load Deformation Behavior of Normalized Carbon Steels Ck15 and Ck45 Under Tensile-Compressive and Rotating-Bending Loading.
Traiser, H.
Kloos, K.H.
Haerterei-Technische Mitteilungen, 1983, 38 (04): : 170 - 179
[39] Abrasive Wear Mechanisms of S235JR, S355J2, C45, AISI 304, and Hardox 500 Steels Tested Using Garnet, Corundum and Carborundum Abrasives
Szala, Miroslaw
Szafran, Michal
Matijosius, Jonas
Drozd, Kazimierz
ADVANCES IN SCIENCE AND TECHNOLOGY-RESEARCH JOURNAL, 2023, 17 (02) : 147 - 160
[40] Comparative Study on Rate of Flow Accelerated Corrosion (FAC) of API 5L X-52-65-70 Steels in a Brine added with H2S at 60°C by Using a Rotating Cylinder Electrode (RCE)
Cervantes Tobon, A.
Diaz Cruz, M.
Gonzalez Velazquez, L.
Godinez Salcedo, J. G.
Macias Salinas, R.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2014, 9 (12): : 6781 - 6792

← 1 2 3 4 →