Evidence for a localized ductile fracture in the 'brittle' transgranular stress corrosion cracking of ductile F.C.C. alloys

被引：0

作者：

Kaufman, M.J. ^{[1
]}

Fink, J.L. ^{[1
]}

机构：

[1] Univ of Washington, United States

来源：

Acta Metallurgica | 1988年 / 36卷 / 08期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Metals and Alloys

引用

页码：2213 / 2228

共 37 条

[21] EFFECT OF THE CHEMICAL-COMPOSITION OF FE-MN-C-P ALLOYS ON THE BRITTLE-DUCTILE TRANSITION-TEMPERATURE IN THE SOLIDIFICATION RANGE
CHOJECKI, A
TELEJKO, I
STEEL RESEARCH, 1992, 63 (10): : 447 - 452
[22] Effect of Grain Size on Ductile-Brittle Transition Behavior of Austenitic Fe-18Cr-10Mn-N-C Alloys
Lee, Sang-In
Lee, Seung-Yong
Nam, Seung Hoon
Hwang, Byoungchul
KOREAN JOURNAL OF MATERIALS RESEARCH, 2015, 25 (10): : 559 - 565
[23] STRESS-CORROSION CRACKING OF IRON AND NICKEL-BASE ALLOYS IN SULFATE SOLUTIONS AT 289 C
VERMILYEA, DA
CORROSION, 1973, 29 (11) : 442 - 448
[24] Non fracture prediction of a C-Mn weld joint in brittle to ductile fracture transition temperature range. Part II: Determination of the stress-based criterion parameters and evaluation of its transferability
Blouin, A.
Chapuliot, S.
Marie, S.
Niclaeys, C.
Bergheau, J. -M.
ENGINEERING FRACTURE MECHANICS, 2016, 156 : 68 - 82
[25] Stacking fault energy (s.f.e.) and grain size effects (d) on the tensile behaviour of f.c.c. polycrystalline alloys at 300 K: Back stress and effective stress evolutions
Haddou, H
Gaudin, C
Feaugas, X
JOURNAL DE PHYSIQUE IV, 2001, 11 (PR4): : 283 - 291
[26] Non-fracture prediction of a C-Mn weld joint in the brittle-to-ductile fracture transition temperature range Part I: Experimental results and numerical study
Niclaeys, C.
N'Guyen, T. H.
Marie, S.
Chapuliot, S.
Degallaix, S.
ENGINEERING FRACTURE MECHANICS, 2012, 79 : 149 - 166
[27] EFFECT OF MANGANESE CONTENT ON STRESS-CORROSION CRACKING SUSCEPTIBILITY OF QUENCHED-AND-TEMPERED FE-C-MN ALLOYS IN SALT WATER
SANDOZ, G
NEWBEGIN, RL
REPORT OF NRL PROGRESS, 1970, : 26 - &
[28] EFFECT OF THERMOMECHANICAL TREATMENT OF 0.45-WT-PERCENT C-STEEL IN THE SUPERPLASTIC MODE ON PLASTIC ZONE PARAMETERS AFTER IMPACT FRACTURE IN THE DUCTILE-BRITTLE TRANSITION-TEMPERATURE RANGE
FARKHUTDINOV, KG
FAIRUSHIN, FA
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 190 (1-2): : 117 - 123
[29] Anodic Stress Corrosion Cracking Suspectibility of Nickel and Nickel-Chromium Alloys Containing Molybdenum and Iron in Bicarbonate Plus Chloride Solutions at 90°C
Zadorozne, N. S.
Giordano, C. M.
Rebak, R. B.
Ares, A. E.
Carranza, R. M.
CORROSION, 2015, 71 (04) : 420 - 432
[30] PREDICTION OF STRESS-CORROSION CRACKING IN 10-PERCENT CAUSTIC SODA SOLUTION AT 315-DEGREES-C (600-DEGREES-F)
PESSALL, N
CORROSION SCIENCE, 1980, 20 (02) : 225 - 242

← 1 2 3 4 →