TESTS OF PERICLASE-CARBON REFRACTORIES IN AN ARC STEEL-MELTING FURNACE.

被引：0

作者：

Suvorov, S.A. ^{[1
]}

Smilovitskii, A.M. ^{[1
]}

Sizov, V.I. ^{[1
]}

Perepelitsyn, A.A. ^{[1
]}

Boriskova, T.I. ^{[1
]}

Beek, K.A. ^{[1
]}

Kiis, K.E. ^{[1
]}

机构：

[1] Leningrad Soviet Leningrad, Polytechnic Inst, Leningrad, USSR, Leningrad Soviet Leningrad Polytechnic Inst, Leningrad, USSR

来源：

Refractories (English translation of Ogneupory) | 1985年 / 26卷 / 9-10期

关键词：

CARBON - REFRACTORY MATERIALS - Magnesite;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Unfired periclase-carbon parts were tested. The average wear rate was 30% less than for PKhS parts. With a decrease in lining thickness from 460 to 230 mm the wear rate dropped. During service a complex infiltration-metasomatic zonality is formed which has an iron-silicate character. In contrast to normal magnesia spinel parts (PShS, MKhS, PKhS) the periclase-carbon refractories have three or four times less thickness of the working zones. In addition there is no transition zone in which loosening and the formation of micro- and macrocracks leading to spalling occur.

引用

页码：571 / 575

共 50 条

[1] TESTS OF PERICLASE-CARBON REFRACTORIES IN AN ARC STEEL-MELTING FURNACE
SUVOROV, SA
SMILOVITSKII, AM
SIZOV, VI
PEREPELITSYN, AA
BORISKOVA, TI
BEEK, KA
KIIS, KE
REFRACTORIES, 1985, 26 (9-10): : 571 - 575
[2] Effect of Force on the Arc in a Steel-Melting Arc Furnace.
Kegel, Kurt
Elektrowaerme International, Edition B: Industrielle Elektrowaerme, 1979, 37 (06): : 300 - 304
[3] PERICLASE-CARBON PRODUCTS FOR ELECTRIC STEEL-MELTING FURNACES.
Khoroshavin, L.B.
Perepelitsyn, V.A.
Turchaninov, V.S.
Mezentsev, E.P.
Bibaev, V.M.
Chuklai, A.M.
Chirikhin, V.F.
Sorokolet, G.P.
Tarynin, N.G.
Refractories (English translation of Ogneupory), 1986, 27 (9-10): : 599 - 603
[4] CALCULATION OF THE ELECTRICAL PARAMETERS OF THE HEAVY-CURRENT ARC OF A STEEL-MELTING FURNACE.
Kazakov, O.A.
Farnasov, G.A.
Dushin, A.N.
Soviet electrical engineering, 1982, 53 (04): : 109 - 113
[5] CARBON AND PERICLASE-CARBON REFRACTORIES
STARON, J
CHEMICKE LISTY, 1992, 86 (08): : 605 - 610
[6] Development of production of periclase-carbon refractories
Entin, V.I.
Aksel'rod, L.M.
Karas', G.E.
Kaplan, F.S.
Rodgol'ts, Yu.S.
Zolotareva, T.I.
Ogneupory i Tekhnicheskaya Keramika, 2001, (01): : 49 - 54
[7] Regulator of electric conditions of arc steel-melting furnace
Gavrilov, E.B.
Kolmakov, S.V.
Suvorov, A.V.
Pribory i Sistemy Upravleniya, 1993, (05):
[8] Decarburization of Periclase-Carbon and Aluminum-Periclase-Carbon Ladle Refractories
Yakushevich N.F.
Zapol’skaya E.M.
Temlyantsev M.V.
Protopopov E.V.
Temlyantseva E.N.
Prikhod’ko M.S.
Steel in Translation, 2022, 52 (08) : 736 - 741
[9] Development of a technology for manufacture of periclase-carbon refractories
Kungurtsev, VN
Mironova, LV
Kochubeev, YN
Borisova, YA
REFRACTORIES AND INDUSTRIAL CERAMICS, 2002, 43 (1-2) : 19 - 21
[10] Experience in the use of periclase-carbon refractories in the working lining of a steel converter
Nagornyi, AP
Buga, ID
Kovura, AB
Kravchenko, AI
Nagornyi, SA
REFRACTORIES AND INDUSTRIAL CERAMICS, 1997, 38 (11-12) : 475 - 478

← 1 2 3 4 5 →