Investigations into Stress Corrosion of High Strength Rope Wires in Condensating Water.

被引：0
|
作者：
Nuernberger, U.
Frey, R.
机构：
来源：
Werkstoffe und Korrosion | 1981年 / 32卷 / 05期
关键词：
Compilation and indexing terms; Copyright 2025 Elsevier Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
CORROSION - Stress Corrosion Cracking
引用
收藏
页码：201 / 211
相关论文
共 50 条
  • [31] A multi-physics coupling analysis to predict stress corrosion characteristics of wires in rope under wear damage
    Wang, Gaofang
    Peng, Yuxing
    Zhu, Zhencai
    Chang, Xiangdong
    Lu, Hao
    Wang, Dagang
    Tang, Wei
    Huang, Kun
    Abdel Wahab, Magd
    Simulation Modelling Practice and Theory, 2024, 131
  • [32] EFFECTS OF DISSOLVED OXYGEN CONCENTRATION AND TEMPERATURE ON THE STRESS CORROSION CRACKING OF LOW ALLOY STEELS IN HIGH TEMPERATURE WATER.
    Kuniya, Jiro
    Kanno, Masayoshi
    Masaoka, Isao
    Sasaki, Ryoichi
    1600, (32):
  • [33] A multi-physics coupling analysis to predict stress corrosion characteristics of wires in rope under wear damage
    Wang, Gaofang
    Peng, Yuxing
    Zhu, Zhencai
    Chang, Xiangdong
    Lu, Hao
    Wang, Dagang
    Tang, Wei
    Huang, Kun
    Wahab, Magd Abdel
    SIMULATION MODELLING PRACTICE AND THEORY, 2024, 131
  • [34] STRESS CORROSION CRACKING SUSCEPTIBILITY OF VARIOUS AUSTENITIC STAINLESS STEEL PIPE WELDS IN HIGH TEMPERATURE OXYGENATED WATER.
    Kuniya, Jiro
    Hattori, Shigeo
    Masaoka, Isao
    Sasaki, Ryoichi
    Ito, Hisao
    Boshoku gijutsu, 1982, 31 (04): : 261 - 267
  • [35] EFFECT OF PRE-STRAIN ON STRESS CORROSION CRACKING OF TYPE 304 STAINLESS STEEL IN HIGH TEMPERATURE WATER.
    Kuniya, Jiro
    Masaoka, Isao
    Sasaki, Ryoichi
    Nakagawa, Yusaku
    Boshoku gijutsu, 1980, 29 (08): : 397 - 402
  • [36] EFFECTS OF ELECTROCHEMICAL POTENTIAL AND FLOW RATE ON CORROSION FATIGUE CRACK GROWTH BEHAVIOR OF HIGH STRENGTH STEEL IN SEA WATER.
    Jang, Soon-Shik
    Shoji, Tetsuo
    Takahashi, Hideaki
    Transactions of the Iron and Steel Institute of Japan, 1986, 27 (05)
  • [37] PROBABILITY DISTRIBUTION OF INTERGRANULAR STRESS CORROSION CRACKING LIFE FOR SENSITIZED 304 STAINLESS STEELS IN HIGH TEMPERATURE, HIGH PURITY WATER.
    Akashi, Masatsune
    Kenjyo, Takao
    Matsukura, Shinji
    Kawamoto, Teruaki
    Boshoku gijutsu, 1984, 33 (11): : 628 - 634
  • [38] EFFECTS OF ENVIRONMENTAL FACTORS AND CYCLIC STRESS ON INTERGRANULAR STRESS CORROSION CRACKING OF SENSITIZED TYPE 304 STAINLESS STEEL IN HIGH TEMPERATURE WATER.
    Ishihara, Tadao
    Ohashi, Shigeo
    Boshoku gijutsu, 1983, 32 (06): : 324 - 330
  • [39] Predicting the fatigue survival probability of High-Strength steel Wires: A Weibull model incorporating corrosion and stress ratios
    Wang, Qianling
    Yao, Guowen
    Yu, Xuanrui
    He, Xuanbo
    Qu, Yuan
    Song, Anxiang
    Zeng, Jianchuan
    ENGINEERING FAILURE ANALYSIS, 2025, 167
  • [40] Influence of tensile stress on corrosion behaviour of high-strength galvanized steel bridge wires in simulated acid rain
    Yang, W. J.
    Yang, P.
    Li, X. M.
    Feng, W. L.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2012, 63 (05): : 401 - 407
12345