Investigations into Stress Corrosion of High Strength Rope Wires in Condensating Water.

被引：0
|
作者：
Nuernberger, U.
Frey, R.
机构：
来源：
Werkstoffe und Korrosion | 1981年 / 32卷 / 05期
关键词：
Compilation and indexing terms; Copyright 2025 Elsevier Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
CORROSION - Stress Corrosion Cracking
引用
收藏
页码：201 / 211
相关论文
共 50 条
  • [1] INVESTIGATIONS INTO STRESS-CORROSION OF HIGH-STRENGTH ROPE WIRES IN CONDENSATING WATER
    NURNBERGER, U
    FREY, R
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1981, 32 (05): : 201 - 211
  • [2] CORROSION FATIGUE OF HIGH STRENGTH STEEL IN SEA FLOWING WATER.
    Jang, Soon-Shik
    Shoji, Tetsuo
    Takahashi, Hideaki
    Watanabe, Yutaka
    1600, (35):
  • [3] Corrosion of High-Strength Steel Wires under Tensile Stress
    Lv, Shanglin
    Li, Kefei
    Chen, Jie
    Li, Xiaobin
    MATERIALS, 2020, 13 (21) : 1 - 16
  • [4] ENVIRONMENTAL ASPECTS OF CARBON STEEL STRESS CORROSION IN HIGH PURITY WATER.
    Indig, M.E.
    Weber, J.E.
    Weinstein, D.
    Corrosion Reviews, 1982, 5 (1-4): : 173 - 225
  • [5] STRESS CORROSION CRACKING SUSCEPTIBILITIES OF VARIOUS STAINLESS STEELS IN HIGH TEMPERATURE WATER.
    Shoji, Saburo
    Ohnaka, Noriyuki
    Kikuchi, Eiji
    Minato, Akira
    Tanno, Kazuo
    Boshoku gijutsu, 1980, 29 (07): : 323 - 329
  • [6] Fatigue Behaviour of High Strength Rope Wires in Corrosive Environments.
    Wiume, D.
    Otto-Graf-Inst, Stuttgart
    Werkstoffe und Korrosion, 1986, 37 (09): : 485 - 493
  • [7] FATIGUE BEHAVIOR OF HIGH-STRENGTH ROPE WIRES IN CORROSIVE ENVIRONMENTS
    WIUME, D
    NURNBERGER, U
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1986, 37 (09): : 485 - 493
  • [8] Bayesian prediction of the stress concentration effect on high-strength wires with corrosion pits
    Guo, Zengwei
    Chen, Hanlin
    Yao, Guowen
    ENGINEERING FAILURE ANALYSIS, 2022, 131
  • [9] Effect of stress ratios on corrosion fatigue life of high-strength steel wires
    Jie, Zhiyu
    Chen, Chao
    Berto, Filippo
    Wang, Kainan
    Peng, Xi
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (02) : 593 - 606
  • [10] STRESS CORROSION CRACKING RESISTANCE OF COMMERCIAL AUSTENITIC STAINLESS STEELS IN HIGH TEMPERATURE WATER.
    Kowaka, Masamichi
    Kobayashi, Taiki
    Kudo, Takeo
    Sumitomo Metals, 1978, 30 (01): : 93 - 101
12345