Effect of Low Temperature on Fatigue Crack Propagation in Weld Joints of 14Kh2GMR Steel under Repeated Shock Loading.

被引：0

|

作者：

Dudin, A.I.

机构：

来源：

| 1600年

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

WELDS

引用

收藏

相关论文

共 41 条

[31] Research on High Temperature Low Cycle Fatigue Crack Propagation of 2.25Cr-1Mo Steel under Complex Stress State
Zhang, Wenxiao
Gao, Guodong
Mu, Guangyu
NATURAL RESOURCES AND SUSTAINABLE DEVELOPMENT, PTS 1-3, 2012, 361-363 : 1422 - 1425
[32] FATIGUE CRACK-PROPAGATION BEHAVIOR UNDER VARIABLE AMPLITUDE LOADING IN THE NEAR-THRESHOLD REGION OF A HIGH-STRENGTH LOW-ALLOY STEEL
HENAFF, G
PETIT, J
JOURNET, B
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1992, 15 (11) : 1155 - 1170
[33] CRACK-PROPAGATION RATES OF SUS-321 STAINLESS-STEEL UNDER HIGH-TEMPERATURE LOW-CYCLE FATIGUE CONDITIONS
YAMAGUCHI, K
KANAZAWA, K
TRANSACTIONS OF NATIONAL RESEARCH INSTITUTE FOR METALS, 1980, 22 (02): : 57 - 64
[34] Effect of interpass temperature on microstructure, impact toughness and fatigue crack propagation in joints welded using the GTAW process on steel ASTM A743-CA6NM
Federal Technological University of Paraná, Ponta Grossa Campus, Coordination of Mechanics, Ponta Grossa
Paraná, Brazil
不详
Paraná, Brazil
不详
Paraná, Brazil
Weld. Int., 6 (433-440):
[35] Investigation of the High-Temperature Low-Cycle fatigue failure characteristics of P91 steel weld joints and their fatigue strength reduction factors under various load control regimes
Zhao, Lei
Song, Yiming
Xu, Lianyong
Han, Yongdian
Hao, Kangda
INTERNATIONAL JOURNAL OF FATIGUE, 2024, 180
[36] Study of Test Temperature Effect on Regularities of Fatigue Crack Propagation in Heat-resistant 15Kh2MFA and 15KhNMFA Steels.
Pokrovskii, V.V.
Skorenko, Yu.S.
Karzov, G.P.
Timofeev, B.T.
Leonov, V.P.
Problemy Prochnosti, 1982, (02):
[37] EFFECT OF THE RESIDUAL STRESSES ON THE CRACK PROPAGATION RATE da/dt AND THE THRESHOLD (KI)th IN THE WELD JOINT OF A LOW ALLOYED HIGH STRENGTH STEEL UNDER CATHODIC PROTECTION IN SEAWATER
Bonte, E.
Habashi, M.
NEW METHODS OF DAMAGE AND FAILURE ANALYSIS OF STRUCTURAL PARTS, 2010, 2010, : 165 - 182
[38] Effect of the pressure-induced phase transformation on the formation of submicrocrystalline structure and low-temperature recrystallization in the 4Kh14N14V2M steel
Voronova, L. M.
Degtyarev, M. V.
Chashchukhina, T. I.
PHYSICS OF METALS AND METALLOGRAPHY, 2012, 113 (06): : 594 - 601
[39] Effect of the pressure-induced phase transformation on the formation of submicrocrystalline structure and low-temperature recrystallization in the 4Kh14N14V2M steel
L. M. Voronova
M. V. Degtyarev
T. I. Chashchukhina
The Physics of Metals and Metallography, 2012, 113 : 594 - 601
[40] FATIGUE THRESHOLD REGIME OF A LOW-ALLOY FERRITIC STEEL UNDER CLOSURE-FREE TESTING CONDITIONS .2. HYSTERESIS IN NEAR-THRESHOLD FATIGUE CRACK-PROPAGATION - AN EXPERIMENTAL ASSESSMENT
VAIDYA, WV
JOURNAL OF TESTING AND EVALUATION, 1992, 20 (03) : 168 - 179

← 1 2 3 4 5 →